- 拉伸强度 [MPa]: 29.3
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 65 | >= 65 | |
| Tensile Strength, Yield | 29.30 MPa | 4249 psi | |
| Elongation at Yield | 565 % | 565 % | |
| 100% Modulus | 0.00270 GPa | 0.392 ksi | |
| 200% Modulus | 0.00580 GPa | 0.841 ksi | |
| 300% Modulus | 0.009701 GPa | 1.407 ksi | |
| Tear Strength | 34.6 kN/m | 197 pli | Die C |
| Compression Set | 31.7 % @Temperature 70.0 °C, Time 79200 sec | 31.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 9.50 min @Temperature 68.3 °C | 0.158 hour @Temperature 155 °F | |