- 拉伸强度 [MPa]: 28.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 64 | >= 64 | |
| Tensile Strength, Yield | 28.10 MPa | 4075 psi | |
| Elongation at Yield | 603 % | 603 % | |
| 100% Modulus | 0.00240 GPa | 0.348 ksi | |
| 200% Modulus | 0.00490 GPa | 0.711 ksi | |
| 300% Modulus | 0.008501 GPa | 1.233 ksi | |
| Tear Strength | 39.9 kN/m | 228 pli | Die C |
| Compression Set | 35.2 % @Temperature 70.0 °C, Time 79200 sec | 35.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.5 min @Temperature 68.3 °C | 0.175 hour @Temperature 155 °F | |