- 拉伸强度 [MPa]: 23.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 80 | >= 80 | |||
| Tensile Strength, Yield | 23.50 MPa | 3408 psi | |||
| Elongation at Yield | 427 % | 427 % | |||
| 100% Modulus | 0.00610 GPa | 0.885 ksi | |||
| 200% Modulus | 0.01300 GPa | 1.885 ksi | |||
| 300% Modulus | 0.0171 GPa | 2.48 ksi | |||
| Tear Strength | 37.7 kN/m | 215 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 53.8 | ||||