- 拉伸强度 [MPa]: 28.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | >= 55 | >= 55 | |||
| Tensile Strength, Yield | 28.10 MPa | 4075 psi | |||
| Elongation at Yield | 623 % | 623 % | |||
| 100% Modulus | 0.00150 GPa | 0.218 ksi | |||
| 200% Modulus | 0.00300 GPa | 0.435 ksi | |||
| 300% Modulus | 0.00560 GPa | 0.812 ksi | |||
| Tear Strength | 40.6 kN/m | 232 pli | Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 10.0 min @Temperature 68.3 °C | 0.167 hour @Temperature 155 °F | Press cured | ||
| Descriptive Properties | |||||
| DIN Abrasion (mm³) | 55.4 | ||||