- 拉伸强度 [MPa]: 28.72
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| 75 | 75 | heat aged 70 hours at 100ºC | |
| Tensile Strength, Yield | 28.72 MPa | 4165 psi | heat aged 70 hours at 100ºC |
| 34.89 MPa | 5061 psi | ||
| Elongation at Yield | 348 % | 348 % | heat aged 70 hours at 100ºC |
| 568 % | 568 % | ||
| 100% Modulus | 0.00292 GPa | 0.424 ksi | |
| 200% Modulus | 0.00654 GPa | 0.949 ksi | |
| 300% Modulus | 0.01202 GPa | 1.744 ksi | |
| Tear Strength | 65.1 kN/m | 371 pli | |
| Compression Set | 65.2 % @Temperature 70.0 °C, Time 79200 sec | 65.2 % @Temperature 158 °F, Time 22.0 hour | heat aged 70 hours at 100ºC |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |