- 拉伸强度 [MPa]: 6.481
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 6.481 MPa @Temperature 24.0 °C | 940.0 psi @Temperature 75.2 °F | Flatwise TS | ||
| 848 MPa @Temperature 24.0 °C | 123000 psi @Temperature 75.2 °F | ||||
| Tensile Modulus | 58.0 GPa @Temperature 24.0 °C | 8410 ksi @Temperature 75.2 °F | |||
| Compressive Yield Strength | 496 MPa @Temperature 71.0 °C | 71900 psi @Temperature 160 °F | |||
| 904 MPa @Temperature 24.0 °C | 131000 psi @Temperature 75.2 °F | ||||
| Compressive Modulus | 57.2 GPa @Temperature 24.0 °C | 8300 ksi @Temperature 75.2 °F | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.022 | Laminate | |||
| Dry Resin Content (%) | 40-44 | Prepreg | |||
| Fiber Volume (%) | 50 | Laminate | |||
| Flow (%) | 4-16 | ||||