- 拉伸强度 [MPa]: 541.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 541 MPa @Temperature 177 °C | 78500 psi @Temperature 351 °F | |||
| 570 MPa @Temperature 24.0 °C | 82700 psi @Temperature 75.2 °F | ||||
| Tensile Modulus | 57.7 GPa @Temperature 177 °C | 8370 ksi @Temperature 351 °F | |||
| 60.7 GPa @Temperature 24.0 °C | 8800 ksi @Temperature 75.2 °F | ||||
| Compressive Yield Strength | 575 MPa @Temperature 71.0 °C | 83400 psi @Temperature 160 °F | |||
| 648 MPa @Temperature 24.0 °C | 94000 psi @Temperature 75.2 °F | ||||
| Shear Strength | 46.0 MPa @Temperature 177 °C | 6670 psi @Temperature 351 °F | Short Beam | ||
| 56.0 MPa @Temperature 132 °C | 8120 psi @Temperature 270 °F | Short Beam | |||
| 72.0 MPa @Temperature -54.0 °C | 10400 psi @Temperature -65.2 °F | Short Beam | |||
| 74.0 MPa @Temperature 24.0 °C | 10700 psi @Temperature 75.2 °F | Short Beam | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.018 | Laminate | |||
| Dry Resin Content (%) | 38-42 | Prepreg | |||
| Fiber Volume (%) | 61 | Laminate | |||
| Flow (%) | 9-22 | ||||