- 熔体流动速率 [g/10min]: 17.0
- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 125.0
- 热变形温度 [℃]: 223.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 116 cm³/g | 116 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Sheet | ||
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm | 0.012 in/in | Sheet | ||
| Melt Flow | 17.0 g/10 min @Load 2.16 kg, Temperature 250 °C | 17.0 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 190 MPa | 27600 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 125 MPa | 18100 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 2.6 % | 2.6 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 8.20 GPa | 1190 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.80 J/cm² | 22.8 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0070 @Frequency 100 Hz | 0.0070 @Frequency 100 Hz | IEC 60250 | ||
| 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 150 V | 150 V | Test solution B; IEC 60112 | ||
| 200 V | 200 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 2.80 - 3.40 µm/m-°C @Temperature 23.0 - 80.0 °C | 1.56 - 1.89 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | ISO 11357-3 | ||
| Maximum Service Temperature, Air | 120 °C | 248 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 130 °C | 266 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | for shrinkage test | ||
| 250 - 275 °C | 482 - 527 °F | Injection molding | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | Natural, Colored, Black and Special Colors | ||||
| Form | Pellets | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| Heat stabilized or stable to heat | |||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||