- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.4
- 弯曲强度 [MPa]: 130.0
- 热变形温度 [℃]: 193.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 132 MPa | 19100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.4 % | 2.4 % | 5mm/min; ISO 527 | ||
| 2.6 % | 2.6 % | ||||
| Tensile Modulus | 8.50 GPa | 1230 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK7110 | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| Heat stabilized or stable to heat | |||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||