- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.4
- 缺口冲击强度: 6.4
- 弯曲强度 [MPa]: 98.0
- 弯曲模量 [MPa]: 5.91
- 热变形温度 [℃]: 208.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 98.0 MPa | 14200 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.8 % | 2.8 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 6.33 GPa | 918 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 5.91 GPa | 857 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 6.40 kJ/m² | 3.05 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.640 J/cm² | 3.05 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| 223 °C | 433 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C | 406 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 168 °C | 334 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK5110 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||