- 密度 [g/cm3]: 1.54
- 弯曲模量 [MPa]: 9.625
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 168 MPa | 24400 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.12 % | 2.12 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 11.12 GPa | 1613 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 246 MPa | 35700 psi | ISO 178 | ||
| Flexural Modulus | 9.625 GPa | 1396 ksi | ISO 178 | ||
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | ISO 179/1eA | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||