- 密度 [g/cm3]: 1.69
- 缺口冲击强度: 0.587
- 弯曲模量 [MPa]: 11.65
- 热变形温度 [℃]: 214.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.69 g/cc | 1.69 g/cc | ASTM D792 | ||
| Density | 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.100 % | 0.100 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00250 - 0.00450 cm/cm | 0.00250 - 0.00450 in/in | ISO 294-4 | ||
| 0.00200 - 0.00500 cm/cm | 0.00200 - 0.00500 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.00600 - 0.00800 cm/cm | 0.00600 - 0.00800 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 77.2 MPa | 11200 psi | ASTM D638 | ||
| 83.0 MPa | 12000 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 1.60 % | 1.60 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 10.8 GPa | 1570 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 131.6 MPa | 19090 psi | ASTM D790 | ||
| 140 MPa | 20300 psi | ISO 178 | |||
| Flexural Modulus | 11.65 GPa | 1690 ksi | ISO 178 | ||
| 7.93 GPa @Temperature 22.8 °C | 1150 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 4.90 kJ/m² | 2.33 ft-lb/in² | ISO 180/1A | ||
| 4.50 kJ/m² @Temperature -30.0 °C | 2.14 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 19.0 kJ/m² | 9.04 ft-lb/in² | ISO 180/1U | ||
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179/1eU | ||
| 2.10 J/cm² @Temperature -30.0 °C | 9.99 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179/1eA | ||
| 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | IEC 60093 | |||
| Surface Resistance | 5.00e+16 ohm | 5.00e+16 ohm | IEC 60093 | ||
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.90 @Frequency 1.00e+6 Hz | 3.90 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.20 @Frequency 100 Hz | 4.20 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 | ||
| 26.4 kV/mm | 670 kV/in | short term; ASTM D149 | |||
| Dissipation Factor | 0.0100 @Frequency 1.00e+6 Hz | 0.0100 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.0190 @Frequency 1.00e+6 Hz | 0.0190 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Arc Resistance | 124 sec | 124 sec | ASTM D495 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| 250 V | 250 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 31.0 µm/m-°C | 17.2 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 46.0 µm/m-°C | 25.6 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 214 °C | 417 °F | ASTM D648 | ||
| 222 °C | 432 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 191 °C | 376 °F | ASTM D648 | ||
| 194 °C | 381 °F | ISO 75-1, -2 | |||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| V-0 @Thickness 0.900 mm | V-0 @Thickness 0.0354 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 96.0 °C | 149 - 205 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Nozzle Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 235 - 255 °C | 455 - 491 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | 7792 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||