Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced物性表参数

Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced

Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced 物性表: Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced物性表及特性介绍,Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced注塑参数详情,如需Celanese CELSTRAN PBT-GF50-08 PBT, 50% Glass Reinforced下载, 可到相关下载区下载

弯曲模量 [MPa]: 15.92

Mechanical Properties	Metric	English	Comments

Tensile Strength at Break	178 MPa	25800 psi	5mm/min; ISO 527-2/1A
Elongation at Break	1.45 %	1.45 %	5mm/min; ISO 527-2/1A
Tensile Modulus	16.64 GPa	2413 ksi	1mm/min; ISO 527-2/1A
Flexural Strength	285 MPa	41300 psi	ISO 178
Flexural Modulus	15.92 GPa	2309 ksi	ISO 178
Charpy Impact, Notched	3.20 J/cm²	15.2 ft-lb/in²	ISO 179/1eA

Processing Properties	Metric	English	Comments
Feed Temperature	20.0 - 50.0 °C	68.0 - 122 °F
Melt Temperature	280 - 300 °C	536 - 572 °F
Mold Temperature	80.0 - 90.0 °C	176 - 194 °F
Dew Point	<= -30.0 °C	<= -22.0 °F	Pre-drying

Descriptive Properties
Injection molding	Yes