- 密度 [g/cm3]: 1.68
- 缺口冲击强度: 0.85
- 弯曲强度 [MPa]: 125.0
- 弯曲模量 [MPa]: 9.70
- 硬度: 118.0
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ASTM Test | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 0.2 in/min; ASTM Test | ||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ISO Data | |||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ASTM Test | |||
| 75.0 MPa @Temperature 80.0 °C | 10900 psi @Temperature 176 °F | ASTM Test | |||
| 75.0 MPa @Temperature 80.0 °C | 10900 psi @Temperature 176 °F | ISO Data | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM Test | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 125 MPa | 18100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 2.0 % | 2.0 % | 0.2 in/min; ASTM Test | |||
| 1.7 % @Temperature -40.0 °C | 1.7 % @Temperature -40.0 °F | ISO Data | |||
| 1.7 % @Temperature -40.0 °C | 1.7 % @Temperature -40.0 °F | ASTM Test | |||
| 4.4 % @Temperature 80.0 °C | 4.4 % @Temperature 176 °F | ISO Data | |||
| 4.4 % @Temperature 80.0 °C | 4.4 % @Temperature 176 °F | ASTM Test | |||
| 5.6 % @Temperature 120 °C | 5.6 % @Temperature 248 °F | ASTM Test | |||
| 5.6 % @Temperature 120 °C | 5.6 % @Temperature 248 °F | ISO Data | |||
| Tensile Modulus | 11.1 GPa | 1610 ksi | 1mm/min; ISO 527 | ||
| 3.71 GPa @Temperature 120 °C | 538 ksi @Temperature 248 °F | ISO Data | |||
| 6.04 GPa @Temperature 80.0 °C | 876 ksi @Temperature 176 °F | ISO Data | |||
| 12.5 GPa @Temperature -40.0 °C | 1810 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 210 MPa | 30500 psi | ASTM Test | ||
| Flexural Modulus | 9.70 GPa | 1410 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.17 mm | 1.59 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 24.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 13.3 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| Flammability, UL94 | V-0 @Thickness 0.300 mm | V-0 @Thickness 0.0118 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| 5VA @Thickness 0.800 mm | 5VA @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-112 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Flame retarding agent | ||||
| UL.UL-C | Yes | ||||