- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 1.1
- 弯曲强度 [MPa]: 180.0
- 弯曲模量 [MPa]: 13.1
- 硬度: 116.0
- 热变形温度 [℃]: 242.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | Melt; ISO 1183 | ||
| 1.70 g/cc | 0.0614 lb/in³ | ISO 1183 | |||
| Viscosity Measurement | 0.52 | 0.52 | Inherent Viscosity | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 116 | 116 | ASTM Test | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 180 MPa | 26100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 16.2 GPa | 2350 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 255 MPa | 37000 psi | ISO Data | ||
| 285 MPa | 41300 psi | ASTM Test | |||
| 110 MPa @Temperature 120 °C | 16000 psi @Temperature 248 °F | ASTM Test | |||
| 370 MPa @Temperature -40.0 °C | 53700 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 13.1 GPa | 1900 ksi | ASTM Test | ||
| 4.69 GPa @Temperature 120 °C | 680 ksi @Temperature 248 °F | ASTM Test | |||
| Izod Impact, Notched | 1.10 J/cm @Thickness 3.17 mm | 2.06 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Unnotched | 9.60 J/cm | 18.0 ft-lb/in | ASTM Test | ||
| Charpy Impact, Notched | 1.15 J/cm² | 5.47 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 22.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 12.2 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C | 12.2 µin/in-°F | ASTM Test | ||
| Specific Heat Capacity | 1.573 J/g-°C | 0.3760 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 245 °C | 473 °F | 10 K/min | ||
| 245 °C | 473 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 242 °C | 468 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75 | ||
| 225 °C | 437 °F | ASTM Test | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 115 °C | 239 °F | Injection molding | ||
| Injection Velocity | 115 mm/sec | 4.53 in/sec | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||