  4. DuPont Performance Polymers Rynite® 415HP NC010 PET

DuPont Performance Polymers Rynite® 415HP NC010 PET

DuPont Performance Polymers Rynite® 415HP NC010 PET 物性表: DuPont Performance Polymers Rynite® 415HP NC010 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 415HP NC010 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 415HP NC010 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.39
  • 吸水率 [%]: 0.24
  • 成型收缩率 [%]: 0.0024
  • 缺口冲击强度: 0.69
  • 弯曲模量 [MPa]: 1.10
  • 硬度: 110.0
  • 热变形温度 [℃]: 235.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.39 g/cc1.39 g/ccASTM D792
Density 1.39 g/cc0.0502 lb/in³ISO 1183
Filler Content 15 %15 %
Water Absorption  0.24 %
@Temperature 23.0 °C		0.24 %
@Temperature 73.4 °F		50%RH,23°C,24h; ASTM D570
 0.25 %
@Temperature 23.0 °C		0.25 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 2.5 %
@Temperature 23.0 °C		2.5 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  47000 cP
@Shear Rate 7000 1/s,
Temperature 315 °C		47000 cP
@Shear Rate 7000 1/s,
Temperature 599 °F		ISO 11443
 57000 cP
@Shear Rate 5000 1/s,
Temperature 315 °C		57000 cP
@Shear Rate 5000 1/s,
Temperature 599 °F		ISO 11443
 59000 cP
@Shear Rate 7000 1/s,
Temperature 295 °C		59000 cP
@Shear Rate 7000 1/s,
Temperature 563 °F		ISO 11443
 71000 cP
@Shear Rate 5000 1/s,
Temperature 295 °C		71000 cP
@Shear Rate 5000 1/s,
Temperature 563 °F		ISO 11443
 76000 cP
@Shear Rate 7000 1/s,
Temperature 275 °C		76000 cP
@Shear Rate 7000 1/s,
Temperature 527 °F		ISO 11443
 92000 cP
@Shear Rate 5000 1/s,
Temperature 275 °C		92000 cP
@Shear Rate 5000 1/s,
Temperature 527 °F		ISO 11443
 94000 cP
@Shear Rate 2000 1/s,
Temperature 315 °C		94000 cP
@Shear Rate 2000 1/s,
Temperature 599 °F		ISO 11443
 120000 cP
@Shear Rate 2000 1/s,
Temperature 295 °C		120000 cP
@Shear Rate 2000 1/s,
Temperature 563 °F		ISO 11443
 138000 cP
@Shear Rate 1000 1/s,
Temperature 315 °C		138000 cP
@Shear Rate 1000 1/s,
Temperature 599 °F		ISO 11443
 152000 cP
@Shear Rate 2000 1/s,
Temperature 275 °C		152000 cP
@Shear Rate 2000 1/s,
Temperature 527 °F		ISO 11443
 166000 cP
@Shear Rate 700 1/s,
Temperature 315 °C		166000 cP
@Shear Rate 700 1/s,
Temperature 599 °F		ISO 11443
 173000 cP
@Shear Rate 1000 1/s,
Temperature 295 °C		173000 cP
@Shear Rate 1000 1/s,
Temperature 563 °F		ISO 11443
 200000 cP
@Shear Rate 500 1/s,
Temperature 315 °C		200000 cP
@Shear Rate 500 1/s,
Temperature 599 °F		ISO 11443
 208000 cP
@Shear Rate 700 1/s,
Temperature 295 °C		208000 cP
@Shear Rate 700 1/s,
Temperature 563 °F		ISO 11443
 220000 cP
@Shear Rate 1000 1/s,
Temperature 275 °C		220000 cP
@Shear Rate 1000 1/s,
Temperature 527 °F		ISO 11443
 248000 cP
@Shear Rate 500 1/s,
Temperature 295 °C		248000 cP
@Shear Rate 500 1/s,
Temperature 563 °F		ISO 11443
 263000 cP
@Shear Rate 700 1/s,
Temperature 275 °C		263000 cP
@Shear Rate 700 1/s,
Temperature 527 °F		ISO 11443
 312000 cP
@Shear Rate 500 1/s,
Temperature 275 °C		312000 cP
@Shear Rate 500 1/s,
Temperature 527 °F		ISO 11443
Linear Mold Shrinkage  0.0024 cm/cm
@Thickness 1.57 mm		0.0024 in/in
@Thickness 0.0618 in		Flow
 0.0040 cm/cm
@Thickness 3.20 mm		0.0040 in/in
@Thickness 0.126 in		Flow
 0.0067 cm/cm
@Thickness 1.57 mm		0.0067 in/in
@Thickness 0.0618 in		Transverse
 0.0095 cm/cm
@Thickness 3.20 mm		0.0095 in/in
@Thickness 0.126 in		Transverse
Linear Mold Shrinkage, Flow 0.0045 cm/cm0.0045 in/inParallel; Annealed; ISO 294-4
 0.0035 cm/cm
@Thickness 2.00 mm		0.0035 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.012 cm/cm0.012 in/inNormal; Annealed; ISO 294-4
 0.0085 cm/cm
@Thickness 2.00 mm		0.0085 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 4.0 g/10 min
@Load 2.16 kg,
Temperature 280 °C		4.0 g/10 min
@Load 4.76 lb,
Temperature 536 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 5555ASTM D785
 5858ISO 2039/2
Hardness, Rockwell R 110110ASTM D785
 111111ISO 2039/2
Tensile Strength at Break 79.0 MPa
@Temperature 23.0 °C		11500 psi
@Temperature 73.4 °F		ISO 527
Tensile Strength  35.9 MPa
@Temperature 150 °C		5210 psi
@Temperature 302 °F		ASTM D638
 44.8 MPa
@Temperature 90.0 °C		6500 psi
@Temperature 194 °F		ASTM D638
 79.0 MPa
@Temperature 23.0 °C		11500 psi
@Temperature 73.4 °F		ASTM D638
 145 MPa
@Temperature -40.0 °C		21000 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  13.4 MPa
@Strain 1.00 %,
Temperature 150 °C		1940 psi
@Strain 1.00 %,
Temperature 302 °F		ISO 527
 16.4 MPa
@Strain 0.450 %,
Temperature 40.0 °C		2380 psi
@Strain 0.450 %,
Temperature 104 °F		ISO 527
 18.1 MPa
@Strain 1.00 %,
Temperature 120 °C		2630 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 18.2 MPa
@Strain 0.350 %,
Temperature 23.0 °C		2640 psi
@Strain 0.350 %,
Temperature 73.4 °F		ISO 527
 19.7 MPa
@Strain 0.300 %,
Temperature 0.000 °C		2860 psi
@Strain 0.300 %,
Temperature 32.0 °F		ISO 527
 21.1 MPa
@Strain 1.00 %,
Temperature 90.0 °C		3060 psi
@Strain 1.00 %,
Temperature 194 °F		ISO 527
 22.0 MPa
@Strain 0.800 %,
Temperature 60.0 °C		3190 psi
@Strain 0.800 %,
Temperature 140 °F		ISO 527
 23.1 MPa
@Strain 2.00 %,
Temperature 150 °C		3350 psi
@Strain 2.00 %,
Temperature 302 °F		ISO 527
 27.9 MPa
@Strain 0.350 %,
Temperature -20.0 °C		4050 psi
@Strain 0.350 %,
Temperature -4.00 °F		ISO 527
 29.7 MPa
@Strain 2.00 %,
Temperature 120 °C		4310 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 30.0 MPa
@Strain 3.00 %,
Temperature 150 °C		4350 psi
@Strain 3.00 %,
Temperature 302 °F		ISO 527
 30.1 MPa
@Strain 0.900 %,
Temperature 40.0 °C		4370 psi
@Strain 0.900 %,
Temperature 104 °F		ISO 527
 33.0 MPa
@Strain 2.00 %,
Temperature 90.0 °C		4790 psi
@Strain 2.00 %,
Temperature 194 °F		ISO 527
 33.2 MPa
@Strain 0.700 %,
Temperature 23.0 °C		4820 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 527
 34.1 MPa
@Strain 4.00 %,
Temperature 150 °C		4950 psi
@Strain 4.00 %,
Temperature 302 °F		ISO 527
 36.4 MPa
@Strain 3.00 %,
Temperature 120 °C		5280 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 527
 36.6 MPa
@Strain 0.600 %,
Temperature 0.000 °C		5310 psi
@Strain 0.600 %,
Temperature 32.0 °F		ISO 527
 37.1 MPa
@Strain 5.00 %,
Temperature 150 °C		5380 psi
@Strain 5.00 %,
Temperature 302 °F		ISO 527
 37.2 MPa
@Strain 1.60 %,
Temperature 60.0 °C		5400 psi
@Strain 1.60 %,
Temperature 140 °F		ISO 527
 38.9 MPa
@Strain 6.00 %,
Temperature 150 °C		5640 psi
@Strain 6.00 %,
Temperature 302 °F		ISO 527
 40.0 MPa
@Strain 7.00 %,
Temperature 150 °C		5800 psi
@Strain 7.00 %,
Temperature 302 °F		ISO 527
 40.2 MPa
@Strain 3.00 %,
Temperature 90.0 °C		5830 psi
@Strain 3.00 %,
Temperature 194 °F		ISO 527
 40.4 MPa
@Strain 4.00 %,
Temperature 120 °C		5860 psi
@Strain 4.00 %,
Temperature 248 °F		ISO 527
 40.8 MPa
@Strain 8.00 %,
Temperature 150 °C		5920 psi
@Strain 8.00 %,
Temperature 302 °F		ISO 527
 41.2 MPa
@Strain 1.35 %,
Temperature 40.0 °C		5980 psi
@Strain 1.35 %,
Temperature 104 °F		ISO 527
 41.4 MPa
@Strain 9.00 %,
Temperature 150 °C		6000 psi
@Strain 9.00 %,
Temperature 302 °F		ISO 527
 41.9 MPa
@Strain 10.0 %,
Temperature 150 °C		6080 psi
@Strain 10.0 %,
Temperature 302 °F		Break; ISO 527
 42.6 MPa
@Strain 5.00 %,
Temperature 120 °C		6180 psi
@Strain 5.00 %,
Temperature 248 °F		ISO 527
 43.7 MPa
@Strain 6.00 %,
Temperature 120 °C		6340 psi
@Strain 6.00 %,
Temperature 248 °F		ISO 527
 44.6 MPa
@Strain 7.00 %,
Temperature 120 °C		6470 psi
@Strain 7.00 %,
Temperature 248 °F		ISO 527
 44.7 MPa
@Strain 4.00 %,
Temperature 90.0 °C		6480 psi
@Strain 4.00 %,
Temperature 194 °F		ISO 527
 45.0 MPa
@Strain 8.00 %,
Temperature 120 °C		6530 psi
@Strain 8.00 %,
Temperature 248 °F		ISO 527
 46.1 MPa
@Strain 9.00 %,
Temperature 120 °C		6690 psi
@Strain 9.00 %,
Temperature 248 °F		ISO 527
 46.5 MPa
@Strain 1.05 %,
Temperature 23.0 °C		6740 psi
@Strain 1.05 %,
Temperature 73.4 °F		ISO 527
 46.6 MPa
@Strain 10.0 %,
Temperature 120 °C		6760 psi
@Strain 10.0 %,
Temperature 248 °F		Break; ISO 527
 47.2 MPa
@Strain 2.40 %,
Temperature 60.0 °C		6850 psi
@Strain 2.40 %,
Temperature 140 °F		ISO 527
 47.6 MPa
@Strain 5.00 %,
Temperature 90.0 °C		6900 psi
@Strain 5.00 %,
Temperature 194 °F		ISO 527
 48.8 MPa
@Strain 6.00 %,
Temperature 90.0 °C		7080 psi
@Strain 6.00 %,
Temperature 194 °F		ISO 527
 49.9 MPa
@Strain 7.00 %,
Temperature 90.0 °C		7240 psi
@Strain 7.00 %,
Temperature 194 °F		ISO 527
 50.2 MPa
@Strain 1.80 %,
Temperature 40.0 °C		7280 psi
@Strain 1.80 %,
Temperature 104 °F		ISO 527
 50.8 MPa
@Strain 8.00 %,
Temperature 90.0 °C		7370 psi
@Strain 8.00 %,
Temperature 194 °F		ISO 527
 51.3 MPa
@Strain 0.900 %,
Temperature 0.000 °C		7440 psi
@Strain 0.900 %,
Temperature 32.0 °F		ISO 527
 51.3 MPa
@Strain 0.700 %,
Temperature -20.0 °C		7440 psi
@Strain 0.700 %,
Temperature -4.00 °F		ISO 527
 51.5 MPa
@Strain 9.00 %,
Temperature 90.0 °C		7470 psi
@Strain 9.00 %,
Temperature 194 °F		ISO 527
 51.9 MPa
@Strain 10.0 %,
Temperature 90.0 °C		7530 psi
@Strain 10.0 %,
Temperature 194 °F		Break; ISO 527
 53.6 MPa
@Strain 3.20 %,
Temperature 60.0 °C		7770 psi
@Strain 3.20 %,
Temperature 140 °F		ISO 527
 57.4 MPa
@Strain 1.40 %,
Temperature 23.0 °C		8330 psi
@Strain 1.40 %,
Temperature 73.4 °F		ISO 527
 57.6 MPa
@Strain 4.00 %,
Temperature 60.0 °C		8350 psi
@Strain 4.00 %,
Temperature 140 °F		ISO 527
 57.7 MPa
@Strain 2.25 %,
Temperature 40.0 °C		8370 psi
@Strain 2.25 %,
Temperature 104 °F		ISO 527
 59.6 MPa
@Strain 4.80 %,
Temperature 60.0 °C		8640 psi
@Strain 4.80 %,
Temperature 140 °F		ISO 527
 60.2 MPa
@Strain 5.60 %,
Temperature 60.0 °C		8730 psi
@Strain 5.60 %,
Temperature 140 °F		ISO 527
 60.6 MPa
@Strain 6.40 %,
Temperature 60.0 °C		8790 psi
@Strain 6.40 %,
Temperature 140 °F		ISO 527
 60.9 MPa
@Strain 7.20 %,
Temperature 60.0 °C		8830 psi
@Strain 7.20 %,
Temperature 140 °F		ISO 527
 61.1 MPa
@Strain 8.00 %,
Temperature 60.0 °C		8860 psi
@Strain 8.00 %,
Temperature 140 °F		Break; ISO 527
 63.5 MPa
@Strain 2.70 %,
Temperature 40.0 °C		9210 psi
@Strain 2.70 %,
Temperature 104 °F		ISO 527
 63.8 MPa
@Strain 1.20 %,
Temperature 0.000 °C		9250 psi
@Strain 1.20 %,
Temperature 32.0 °F		ISO 527
 66.0 MPa
@Strain 1.75 %,
Temperature 23.0 °C		9570 psi
@Strain 1.75 %,
Temperature 73.4 °F		ISO 527
 67.5 MPa
@Strain 3.15 %,
Temperature 40.0 °C		9790 psi
@Strain 3.15 %,
Temperature 104 °F		ISO 527
 69.9 MPa
@Strain 3.60 %,
Temperature 40.0 °C		10100 psi
@Strain 3.60 %,
Temperature 104 °F		ISO 527
 70.6 MPa
@Strain 1.05 %,
Temperature -20.0 °C		10200 psi
@Strain 1.05 %,
Temperature -4.00 °F		ISO 527
 71.1 MPa
@Strain 4.05 %,
Temperature 40.0 °C		10300 psi
@Strain 4.05 %,
Temperature 104 °F		ISO 527
 71.3 MPa
@Strain 4.50 %,
Temperature 40.0 °C		10300 psi
@Strain 4.50 %,
Temperature 104 °F		Break; ISO 527
 72.7 MPa
@Strain 2.10 %,
Temperature 23.0 °C		10500 psi
@Strain 2.10 %,
Temperature 73.4 °F		ISO 527
 74.6 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10800 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 77.6 MPa
@Strain 2.45 %,
Temperature 23.0 °C		11300 psi
@Strain 2.45 %,
Temperature 73.4 °F		ISO 527
 81.0 MPa
@Strain 2.80 %,
Temperature 23.0 °C		11700 psi
@Strain 2.80 %,
Temperature 73.4 °F		ISO 527
 83.3 MPa
@Strain 3.15 %,
Temperature 23.0 °C		12100 psi
@Strain 3.15 %,
Temperature 73.4 °F		ISO 527
 83.8 MPa
@Strain 1.80 %,
Temperature 0.000 °C		12200 psi
@Strain 1.80 %,
Temperature 32.0 °F		ISO 527
 84.5 MPa
@Strain 3.50 %,
Temperature 23.0 °C		12300 psi
@Strain 3.50 %,
Temperature 73.4 °F		Break; ISO 527
 86.3 MPa
@Strain 1.40 %,
Temperature -20.0 °C		12500 psi
@Strain 1.40 %,
Temperature -4.00 °F		ISO 527
 91.6 MPa
@Strain 2.10 %,
Temperature 0.000 °C		13300 psi
@Strain 2.10 %,
Temperature 32.0 °F		ISO 527
 98.2 MPa
@Strain 2.40 %,
Temperature 0.000 °C		14200 psi
@Strain 2.40 %,
Temperature 32.0 °F		ISO 527
 98.9 MPa
@Strain 1.75 %,
Temperature -20.0 °C		14300 psi
@Strain 1.75 %,
Temperature -4.00 °F		ISO 527
 104 MPa
@Strain 2.70 %,
Temperature 0.000 °C		15100 psi
@Strain 2.70 %,
Temperature 32.0 °F		ISO 527
 109 MPa
@Strain 3.00 %,
Temperature 0.000 °C		15800 psi
@Strain 3.00 %,
Temperature 32.0 °F		Break; ISO 527
 109 MPa
@Strain 2.10 %,
Temperature -20.0 °C		15800 psi
@Strain 2.10 %,
Temperature -4.00 °F		ISO 527
 116 MPa
@Strain 2.45 %,
Temperature -20.0 °C		16800 psi
@Strain 2.45 %,
Temperature -4.00 °F		ISO 527
 122 MPa
@Strain 2.80 %,
Temperature -20.0 °C		17700 psi
@Strain 2.80 %,
Temperature -4.00 °F		ISO 527
 126 MPa
@Strain 3.15 %,
Temperature -20.0 °C		18300 psi
@Strain 3.15 %,
Temperature -4.00 °F		ISO 527
 128 MPa
@Strain 3.33 %,
Temperature -20.0 °C		18600 psi
@Strain 3.33 %,
Temperature -4.00 °F		Break; ISO 527
Elongation at Break  3.0 %
@Temperature -40.0 °C		3.0 %
@Temperature -40.0 °F		ASTM D638
 5.0 %
@Temperature 23.0 °C		5.0 %
@Temperature 73.4 °F		ISO 527
 6.0 %
@Temperature 23.0 °C		6.0 %
@Temperature 73.4 °F		ASTM D638
 13 %
@Temperature 90.0 °C		13 %
@Temperature 194 °F		ASTM D638
 14 %
@Temperature 150 °C		14 %
@Temperature 302 °F		ASTM D638
Tensile Modulus  1.69 GPa
@Temperature 150 °C		245 ksi
@Temperature 302 °F		ASTM D638
 1.83 GPa
@Temperature 90.0 °C		265 ksi
@Temperature 194 °F		ASTM D638
 4.22 GPa
@Temperature 23.0 °C		612 ksi
@Temperature 73.4 °F		ASTM D638
 4.70 GPa
@Temperature 23.0 °C		682 ksi
@Temperature 73.4 °F		ISO 527
 6.40 GPa
@Temperature -40.0 °C		928 ksi
@Temperature -40.0 °F		ASTM D638
Flexural Strength  34.5 MPa
@Temperature 150 °C		5000 psi
@Temperature 302 °F		ASTM D790
 48.3 MPa
@Temperature 90.0 °C		7010 psi
@Temperature 194 °F		ASTM D790
 93.1 MPa
@Temperature 23.0 °C		13500 psi
@Temperature 73.4 °F		ASTM D790
 210 MPa
@Temperature -40.0 °C		30500 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  1.10 GPa
@Temperature 150 °C		160 ksi
@Temperature 302 °F		ASTM D790
 1.10 GPa
@Temperature 150 °C		160 ksi
@Temperature 302 °F		ISO 178
 1.28 GPa
@Temperature 90.0 °C		186 ksi
@Temperature 194 °F		ASTM D790
 1.30 GPa
@Temperature 93.0 °C		189 ksi
@Temperature 199 °F		ISO 178
 3.55 GPa
@Temperature 23.0 °C		515 ksi
@Temperature 73.4 °F		ISO 178
 3.60 GPa
@Temperature 23.0 °C		522 ksi
@Temperature 73.4 °F		ASTM D790
 5.86 GPa
@Temperature -40.0 °C		850 ksi
@Temperature -40.0 °F		ASTM D790
 5.90 GPa
@Temperature -40.0 °C		856 ksi
@Temperature -40.0 °F		ISO 178
Compressive Strength 93.0 MPa
@Temperature 23.0 °C		13500 psi
@Temperature 73.4 °F		ASTM D695
Shear Strength 40.0 MPa
@Temperature 23.0 °C		5800 psi
@Temperature 73.4 °F		ASTM D732
Izod Impact, Notched  0.690 J/cm
@Temperature -40.0 °C		1.29 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  6.40 J/cm
@Temperature -40.0 °C		12.0 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 8.55 J/cm
@Temperature 23.0 °C		16.0 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  7.70 kJ/m²
@Temperature -30.0 °C		3.66 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 13.0 kJ/m²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched  2.50 J/cm²
@Temperature -30.0 °C		11.9 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 5.50 J/cm²
@Temperature 23.0 °C		26.2 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.800 J/cm²
@Temperature -30.0 °C		3.81 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.10 J/cm²
@Temperature 23.0 °C		5.23 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+11 ohm-cm
@Temperature 23.0 °C		1.00e+11 ohm-cm
@Temperature 73.4 °F		ASTM D257
 1.00e+13 ohm-cm
@Temperature 23.0 °C		1.00e+13 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance  1.00e+13 ohm
@Temperature 23.0 °C		1.00e+13 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+13 ohm
@Temperature 23.0 °C		1.00e+13 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.7
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.7
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.9
@Frequency 1000 Hz,
Temperature 23.0 °C		3.9
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
Dielectric Strength 39.0 kV/mm
@Temperature 23.0 °C		991 kV/in
@Temperature 73.4 °F		IEC 60243-1
 6.50 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		165 kV/in
@Thickness 0.126 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 8.50 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		216 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 11.0 kV/mm
@Thickness 3.20 mm,
Temperature 95.0 °C		279 kV/in
@Thickness 0.126 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 15.5 kV/mm
@Thickness 1.60 mm,
Temperature 95.0 °C		394 kV/in
@Thickness 0.0630 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 18.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		457 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 24.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		610 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
Dissipation Factor  0.019
@Frequency 1000 Hz,
Temperature 23.0 °C		0.019
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.022
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.022
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
Comparative Tracking Index  250 - 400 V
@Temperature 23.0 °C		250 - 400 V
@Temperature 73.4 °F		UL 746A
 350 V
@Temperature 23.0 °C		350 V
@Temperature 73.4 °F		IEC 60112
 275 V
@Thickness 3.00 mm,
Temperature 23.0 °C		275 V
@Thickness 0.118 in,
Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  98.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		54.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 98.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		54.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 109 µm/m-°C
@Temperature 55.0 - 160 °C		60.6 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 109 µm/m-°C
@Temperature 55.0 - 160 °C		60.6 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 117 µm/m-°C
@Temperature 23.0 - 55.0 °C		65.0 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 130 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		72.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 130 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		72.2 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 250 °C482 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 235 °C455 °FISO 75-1/-2
 235 °C455 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C405 °FISO 75-1/-2
 207 °C405 °FASTM D648
UL RTI, Electrical  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
UL RTI, Mechanical with Impact  120 °C
@Thickness 0.750 mm		248 °F
@Thickness 0.0295 in		UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		UL 746B
 120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
Oxygen Index 19 %19 %ASTM D2863
 19 %19 %ISO 4589-1/-2
Glow Wire Test  675 °C
@Thickness 0.750 mm		1250 °F
@Thickness 0.0295 in		IEC 60695-2-12
 675 °C
@Thickness 1.50 mm		1250 °F
@Thickness 0.0591 in		IEC 60695-2-12
 700 °C
@Thickness 0.750 mm		1290 °F
@Thickness 0.0295 in		Ignition; IEC 60695-2-13
 700 °C
@Thickness 1.50 mm		1290 °F
@Thickness 0.0591 in		Ignition; IEC 60695-2-13
 750 °C
@Thickness 3.00 mm		1380 °F
@Thickness 0.118 in		IEC 60695-2-12
 775 °C
@Thickness 3.00 mm		1430 °F
@Thickness 0.118 in		Ignition; IEC 60695-2-13
 
Processing PropertiesMetricEnglishComments
Melt Temperature 250 °C482 °F10°C/min; ISO 11357-1/-3
 280 °C536 °FOptimum
 270 - 290 °C518 - 554 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AdditiveImpact Modifier
AppearanceNatural Color
Drying RecommendedYes
FeaturesFlow, Good
 Impact Modified
 Impact Resistance, Good
 Stiffness, Good
 Strength, Good
 Thermal Aging Resistance, Good
FillerGlass fiber reinforcement
FormsPellets
 Pellets
GenericPET
Heat StabilizedYes
Material StatusCurrent
Part Marking Code>PET-IGF15<ISO 11469
Polymer FamilyPolyester
Polymer TypePET
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Toughened Resins
Region Available - GlobalYes
Resin IdentificationPET-IGF15ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesElectrical/Electronic Applications
 Housings
 Parts, Thin-walled

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38897.html

免责声明: 本文 DuPont Performance Polymers Rynite® 415HP NC010 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4