  4. DuPont Performance Polymers Rynite® 935SUV BK593 PET

DuPont Performance Polymers Rynite® 935SUV BK593 PET

DuPont Performance Polymers Rynite® 935SUV BK593 PET 物性表: DuPont Performance Polymers Rynite® 935SUV BK593 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 935SUV BK593 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 935SUV BK593 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.57
 
Physical PropertiesMetricEnglishComments
Density 1.57 g/cc0.0567 lb/in³ISO 1183
Filler Content 35 %35 %
Linear Mold Shrinkage, Flow 0.0030 cm/cm
@Thickness 2.00 mm		0.0030 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 80.0 MPa
@Temperature 23.0 °C		11600 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  0.410 MPa
@Strain 0.000 %,
Temperature 120 °C		59.5 psi
@Strain 0.000 %,
Temperature 248 °F		ISO 11403-1/-2
 0.480 MPa
@Strain 0.000 %,
Temperature 150 °C		69.6 psi
@Strain 0.000 %,
Temperature 302 °F		ISO 11403-1/-2
 0.730 MPa
@Strain 0.000 %,
Temperature 90.0 °C		106 psi
@Strain 0.000 %,
Temperature 194 °F		ISO 11403-1/-2
 1.41 MPa
@Strain 0.000 %,
Temperature 60.0 °C		205 psi
@Strain 0.000 %,
Temperature 140 °F		ISO 11403-1/-2
 1.69 MPa
@Strain 0.000 %,
Temperature 40.0 °C		245 psi
@Strain 0.000 %,
Temperature 104 °F		ISO 11403-1/-2
 1.77 MPa
@Strain 0.000 %,
Temperature 23.0 °C		257 psi
@Strain 0.000 %,
Temperature 73.4 °F		ISO 11403-1/-2
 1.80 MPa
@Strain 0.0700 %,
Temperature 120 °C		261 psi
@Strain 0.0700 %,
Temperature 248 °F		ISO 11403-1/-2
 1.89 MPa
@Strain 0.000 %,
Temperature 0.000 °C		274 psi
@Strain 0.000 %,
Temperature 32.0 °F		ISO 11403-1/-2
 1.94 MPa
@Strain 0.0700 %,
Temperature 150 °C		281 psi
@Strain 0.0700 %,
Temperature 302 °F		ISO 11403-1/-2
 2.03 MPa
@Strain 0.000 %,
Temperature -20.0 °C		294 psi
@Strain 0.000 %,
Temperature -4.00 °F		ISO 11403-1/-2
 2.05 MPa
@Strain 0.000 %,
Temperature -40.0 °C		297 psi
@Strain 0.000 %,
Temperature -40.0 °F		ISO 11403-1/-2
 2.36 MPa
@Strain 0.0400 %,
Temperature 90.0 °C		342 psi
@Strain 0.0400 %,
Temperature 194 °F		ISO 11403-1/-2
 2.79 MPa
@Strain 0.0300 %,
Temperature 0.000 °C		405 psi
@Strain 0.0300 %,
Temperature 32.0 °F		ISO 11403-1/-2
 3.06 MPa
@Strain 0.120 %,
Temperature 120 °C		444 psi
@Strain 0.120 %,
Temperature 248 °F		ISO 11403-1/-2
 3.30 MPa
@Strain 0.0300 %,
Temperature 60.0 °C		479 psi
@Strain 0.0300 %,
Temperature 140 °F		ISO 11403-1/-2
 3.32 MPa
@Strain 0.140 %,
Temperature 150 °C		482 psi
@Strain 0.140 %,
Temperature 302 °F		ISO 11403-1/-2
 3.34 MPa
@Strain 0.0600 %,
Temperature 0.000 °C		484 psi
@Strain 0.0600 %,
Temperature 32.0 °F		ISO 11403-1/-2
 3.57 MPa
@Strain 0.0300 %,
Temperature -20.0 °C		518 psi
@Strain 0.0300 %,
Temperature -4.00 °F		ISO 11403-1/-2
 3.84 MPa
@Strain 0.0300 %,
Temperature 40.0 °C		557 psi
@Strain 0.0300 %,
Temperature 104 °F		ISO 11403-1/-2
 3.89 MPa
@Strain 0.0400 %,
Temperature -40.0 °C		564 psi
@Strain 0.0400 %,
Temperature -40.0 °F		ISO 11403-1/-2
 3.96 MPa
@Strain 0.0900 %,
Temperature 90.0 °C		574 psi
@Strain 0.0900 %,
Temperature 194 °F		ISO 11403-1/-2
 4.05 MPa
@Strain 0.0600 %,
Temperature -20.0 °C		587 psi
@Strain 0.0600 %,
Temperature -4.00 °F		ISO 11403-1/-2
 4.26 MPa
@Strain 0.0600 %,
Temperature -40.0 °C		618 psi
@Strain 0.0600 %,
Temperature -40.0 °F		ISO 11403-1/-2
 4.27 MPa
@Strain 0.170 %,
Temperature 120 °C		619 psi
@Strain 0.170 %,
Temperature 248 °F		ISO 11403-1/-2
 4.27 MPa
@Strain 0.0300 %,
Temperature 23.0 °C		619 psi
@Strain 0.0300 %,
Temperature 73.4 °F		ISO 11403-1/-2
 4.56 MPa
@Strain 0.200 %,
Temperature 150 °C		661 psi
@Strain 0.200 %,
Temperature 302 °F		ISO 11403-1/-2
 5.24 MPa
@Strain 0.0500 %,
Temperature 60.0 °C		760 psi
@Strain 0.0500 %,
Temperature 140 °F		ISO 11403-1/-2
 5.46 MPa
@Strain 0.230 %,
Temperature 120 °C		792 psi
@Strain 0.230 %,
Temperature 248 °F		ISO 11403-1/-2
 5.47 MPa
@Strain 0.130 %,
Temperature 90.0 °C		793 psi
@Strain 0.130 %,
Temperature 194 °F		ISO 11403-1/-2
 6.17 MPa
@Strain 0.0500 %,
Temperature 40.0 °C		895 psi
@Strain 0.0500 %,
Temperature 104 °F		ISO 11403-1/-2
 6.18 MPa
@Strain 0.0800 %,
Temperature 0.000 °C		896 psi
@Strain 0.0800 %,
Temperature 32.0 °F		ISO 11403-1/-2
 6.42 MPa
@Strain 0.290 %,
Temperature 150 °C		931 psi
@Strain 0.290 %,
Temperature 302 °F		ISO 11403-1/-2
 6.93 MPa
@Strain 0.170 %,
Temperature 90.0 °C		1010 psi
@Strain 0.170 %,
Temperature 194 °F		ISO 11403-1/-2
 6.94 MPa
@Strain 0.0600 %,
Temperature 23.0 °C		1010 psi
@Strain 0.0600 %,
Temperature 73.4 °F		ISO 11403-1/-2
 7.19 MPa
@Strain 0.0900 %,
Temperature -20.0 °C		1040 psi
@Strain 0.0900 %,
Temperature -4.00 °F		ISO 11403-1/-2
 7.21 MPa
@Strain 0.0800 %,
Temperature 60.0 °C		1050 psi
@Strain 0.0800 %,
Temperature 140 °F		ISO 11403-1/-2
 7.74 MPa
@Strain 0.0900 %,
Temperature -40.0 °C		1120 psi
@Strain 0.0900 %,
Temperature -40.0 °F		ISO 11403-1/-2
 8.28 MPa
@Strain 0.210 %,
Temperature 90.0 °C		1200 psi
@Strain 0.210 %,
Temperature 194 °F		ISO 11403-1/-2
 8.33 MPa
@Strain 0.0800 %,
Temperature 40.0 °C		1210 psi
@Strain 0.0800 %,
Temperature 104 °F		ISO 11403-1/-2
 8.95 MPa
@Strain 0.110 %,
Temperature 0.000 °C		1300 psi
@Strain 0.110 %,
Temperature 32.0 °F		ISO 11403-1/-2
 9.13 MPa
@Strain 0.120 %,
Temperature 60.0 °C		1320 psi
@Strain 0.120 %,
Temperature 140 °F		ISO 11403-1/-2
 9.14 MPa
@Strain 0.390 %,
Temperature 120 °C		1330 psi
@Strain 0.390 %,
Temperature 248 °F		ISO 11403-1/-2
 9.40 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		1360 psi
@Strain 0.0800 %,
Temperature 73.4 °F		ISO 11403-1/-2
 9.98 MPa
@Strain 0.270 %,
Temperature 90.0 °C		1450 psi
@Strain 0.270 %,
Temperature 194 °F		ISO 11403-1/-2
 10.36 MPa
@Strain 0.110 %,
Temperature -20.0 °C		1503 psi
@Strain 0.110 %,
Temperature -4.00 °F		ISO 11403-1/-2
 10.74 MPa
@Strain 0.100 %,
Temperature 40.0 °C		1558 psi
@Strain 0.100 %,
Temperature 104 °F		ISO 11403-1/-2
 10.94 MPa
@Strain 0.150 %,
Temperature 60.0 °C		1587 psi
@Strain 0.150 %,
Temperature 140 °F		ISO 11403-1/-2
 11.09 MPa
@Strain 0.110 %,
Temperature -40.0 °C		1608 psi
@Strain 0.110 %,
Temperature -40.0 °F		ISO 11403-1/-2
 11.53 MPa
@Strain 0.620 %,
Temperature 150 °C		1672 psi
@Strain 0.620 %,
Temperature 302 °F		ISO 11403-1/-2
 11.74 MPa
@Strain 0.140 %,
Temperature 0.000 °C		1703 psi
@Strain 0.140 %,
Temperature 32.0 °F		ISO 11403-1/-2
 11.87 MPa
@Strain 0.110 %,
Temperature 23.0 °C		1722 psi
@Strain 0.110 %,
Temperature 73.4 °F		ISO 11403-1/-2
 12.77 MPa
@Strain 0.180 %,
Temperature 60.0 °C		1852 psi
@Strain 0.180 %,
Temperature 140 °F		ISO 11403-1/-2
 12.97 MPa
@Strain 0.130 %,
Temperature 40.0 °C		1881 psi
@Strain 0.130 %,
Temperature 104 °F		ISO 11403-1/-2
 13.44 MPa
@Strain 0.140 %,
Temperature -20.0 °C		1949 psi
@Strain 0.140 %,
Temperature -4.00 °F		ISO 11403-1/-2
 14.03 MPa
@Strain 0.660 %,
Temperature 120 °C		2035 psi
@Strain 0.660 %,
Temperature 248 °F		ISO 11403-1/-2
 14.36 MPa
@Strain 0.130 %,
Temperature 23.0 °C		2083 psi
@Strain 0.130 %,
Temperature 73.4 °F		ISO 11403-1/-2
 14.49 MPa
@Strain 0.130 %,
Temperature -40.0 °C		2102 psi
@Strain 0.130 %,
Temperature -40.0 °F		ISO 11403-1/-2
 14.57 MPa
@Strain 0.210 %,
Temperature 60.0 °C		2113 psi
@Strain 0.210 %,
Temperature 140 °F		ISO 11403-1/-2
 14.67 MPa
@Strain 0.160 %,
Temperature 0.000 °C		2128 psi
@Strain 0.160 %,
Temperature 32.0 °F		ISO 11403-1/-2
 15.12 MPa
@Strain 0.950 %,
Temperature 150 °C		2193 psi
@Strain 0.950 %,
Temperature 302 °F		ISO 11403-1/-2
 15.16 MPa
@Strain 0.150 %,
Temperature 40.0 °C		2199 psi
@Strain 0.150 %,
Temperature 104 °F		ISO 11403-1/-2
 16.19 MPa
@Strain 0.230 %,
Temperature 60.0 °C		2348 psi
@Strain 0.230 %,
Temperature 140 °F		ISO 11403-1/-2
 16.53 MPa
@Strain 0.170 %,
Temperature -20.0 °C		2397 psi
@Strain 0.170 %,
Temperature -4.00 °F		ISO 11403-1/-2
 16.81 MPa
@Strain 0.150 %,
Temperature 23.0 °C		2438 psi
@Strain 0.150 %,
Temperature 73.4 °F		ISO 11403-1/-2
 16.97 MPa
@Strain 0.480 %,
Temperature 90.0 °C		2461 psi
@Strain 0.480 %,
Temperature 194 °F		ISO 11403-1/-2
 17.22 MPa
@Strain 0.180 %,
Temperature 40.0 °C		2498 psi
@Strain 0.180 %,
Temperature 104 °F		ISO 11403-1/-2
 17.54 MPa
@Strain 0.190 %,
Temperature 0.000 °C		2544 psi
@Strain 0.190 %,
Temperature 32.0 °F		ISO 11403-1/-2
 17.71 MPa
@Strain 1.30 %,
Temperature 150 °C		2569 psi
@Strain 1.30 %,
Temperature 302 °F		ISO 11403-1/-2
 17.74 MPa
@Strain 0.160 %,
Temperature -40.0 °C		2573 psi
@Strain 0.160 %,
Temperature -40.0 °F		ISO 11403-1/-2
 18.07 MPa
@Strain 0.970 %,
Temperature 120 °C		2621 psi
@Strain 0.970 %,
Temperature 248 °F		ISO 11403-1/-2
 19.23 MPa
@Strain 0.180 %,
Temperature 23.0 °C		2789 psi
@Strain 0.180 %,
Temperature 73.4 °F		ISO 11403-1/-2
 19.28 MPa
@Strain 0.200 %,
Temperature 40.0 °C		2796 psi
@Strain 0.200 %,
Temperature 104 °F		ISO 11403-1/-2
 19.53 MPa
@Strain 0.190 %,
Temperature -20.0 °C		2833 psi
@Strain 0.190 %,
Temperature -4.00 °F		ISO 11403-1/-2
 19.67 MPa
@Strain 1.67 %,
Temperature 150 °C		2853 psi
@Strain 1.67 %,
Temperature 302 °F		ISO 11403-1/-2
 20.33 MPa
@Strain 0.210 %,
Temperature 0.000 °C		2949 psi
@Strain 0.210 %,
Temperature 32.0 °F		ISO 11403-1/-2
 20.73 MPa
@Strain 0.190 %,
Temperature -40.0 °C		3007 psi
@Strain 0.190 %,
Temperature -40.0 °F		ISO 11403-1/-2
 21.07 MPa
@Strain 2.08 %,
Temperature 150 °C		3056 psi
@Strain 2.08 %,
Temperature 302 °F		ISO 11403-1/-2
 21.1 MPa
@Strain 1.28 %,
Temperature 120 °C		3060 psi
@Strain 1.28 %,
Temperature 248 °F		ISO 11403-1/-2
 21.1 MPa
@Strain 0.310 %,
Temperature 60.0 °C		3060 psi
@Strain 0.310 %,
Temperature 140 °F		ISO 11403-1/-2
 21.3 MPa
@Strain 0.230 %,
Temperature 40.0 °C		3090 psi
@Strain 0.230 %,
Temperature 104 °F		ISO 11403-1/-2
 21.49 MPa
@Strain 0.200 %,
Temperature 23.0 °C		3117 psi
@Strain 0.200 %,
Temperature 73.4 °F		ISO 11403-1/-2
 22.09 MPa
@Strain 2.48 %,
Temperature 150 °C		3204 psi
@Strain 2.48 %,
Temperature 302 °F		ISO 11403-1/-2
 22.24 MPa
@Strain 0.700 %,
Temperature 90.0 °C		3226 psi
@Strain 0.700 %,
Temperature 194 °F		ISO 11403-1/-2
 22.46 MPa
@Strain 0.220 %,
Temperature -20.0 °C		3258 psi
@Strain 0.220 %,
Temperature -4.00 °F		ISO 11403-1/-2
 22.91 MPa
@Strain 2.92 %,
Temperature 150 °C		3323 psi
@Strain 2.92 %,
Temperature 302 °F		ISO 11403-1/-2
 23.01 MPa
@Strain 0.240 %,
Temperature 0.000 °C		3337 psi
@Strain 0.240 %,
Temperature 32.0 °F		ISO 11403-1/-2
 23.21 MPa
@Strain 0.250 %,
Temperature 40.0 °C		3366 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 11403-1/-2
 23.27 MPa
@Strain 1.58 %,
Temperature 120 °C		3375 psi
@Strain 1.58 %,
Temperature 248 °F		ISO 11403-1/-2
 23.53 MPa
@Strain 3.35 %,
Temperature 150 °C		3413 psi
@Strain 3.35 %,
Temperature 302 °F		ISO 11403-1/-2
 23.84 MPa
@Strain 0.220 %,
Temperature -40.0 °C		3458 psi
@Strain 0.220 %,
Temperature -40.0 °F		ISO 11403-1/-2
 23.9 MPa
@Strain 0.230 %,
Temperature 23.0 °C		3470 psi
@Strain 0.230 %,
Temperature 73.4 °F		ISO 11403-1/-2
 24.07 MPa
@Strain 3.78 %,
Temperature 150 °C		3491 psi
@Strain 3.78 %,
Temperature 302 °F		ISO 11403-1/-2
 24.53 MPa
@Strain 4.24 %,
Temperature 150 °C		3558 psi
@Strain 4.24 %,
Temperature 302 °F		ISO 11403-1/-2
 24.94 MPa
@Strain 4.68 %,
Temperature 150 °C		3617 psi
@Strain 4.68 %,
Temperature 302 °F		ISO 11403-1/-2
 25.02 MPa
@Strain 1.92 %,
Temperature 120 °C		3629 psi
@Strain 1.92 %,
Temperature 248 °F		ISO 11403-1/-2
 25.3 MPa
@Strain 5.13 %,
Temperature 150 °C		3670 psi
@Strain 5.13 %,
Temperature 302 °F		ISO 11403-1/-2
 25.37 MPa
@Strain 0.240 %,
Temperature -20.0 °C		3680 psi
@Strain 0.240 %,
Temperature -4.00 °F		ISO 11403-1/-2
 25.62 MPa
@Strain 5.57 %,
Temperature 150 °C		3716 psi
@Strain 5.57 %,
Temperature 302 °F		ISO 11403-1/-2
 25.91 MPa
@Strain 6.01 %,
Temperature 150 °C		3758 psi
@Strain 6.01 %,
Temperature 302 °F		ISO 11403-1/-2
 25.99 MPa
@Strain 0.250 %,
Temperature 23.0 °C		3770 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 11403-1/-2
 26.19 MPa
@Strain 6.46 %,
Temperature 150 °C		3799 psi
@Strain 6.46 %,
Temperature 302 °F		ISO 11403-1/-2
 26.32 MPa
@Strain 2.27 %,
Temperature 120 °C		3817 psi
@Strain 2.27 %,
Temperature 248 °F		ISO 11403-1/-2
 26.44 MPa
@Strain 6.87 %,
Temperature 150 °C		3835 psi
@Strain 6.87 %,
Temperature 302 °F		ISO 11403-1/-2
 26.53 MPa
@Strain 0.920 %,
Temperature 90.0 °C		3848 psi
@Strain 0.920 %,
Temperature 194 °F		ISO 11403-1/-2
 26.61 MPa
@Strain 0.230 %,
Temperature -40.0 °C		3859 psi
@Strain 0.230 %,
Temperature -40.0 °F		ISO 11403-1/-2
 26.66 MPa
@Strain 7.33 %,
Temperature 150 °C		3867 psi
@Strain 7.33 %,
Temperature 302 °F		ISO 11403-1/-2
 26.74 MPa
@Strain 8.76 %,
Temperature 150 °C		3878 psi
@Strain 8.76 %,
Temperature 302 °F		ISO 11403-1/-2
 26.83 MPa
@Strain 7.77 %,
Temperature 150 °C		3891 psi
@Strain 7.77 %,
Temperature 302 °F		ISO 11403-1/-2
 27.0 MPa
@Strain 8.23 %,
Temperature 150 °C		3920 psi
@Strain 8.23 %,
Temperature 302 °F		ISO 11403-1/-2
 27.33 MPa
@Strain 2.63 %,
Temperature 120 °C		3964 psi
@Strain 2.63 %,
Temperature 248 °F		ISO 11403-1/-2
 28.1 MPa
@Strain 3.01 %,
Temperature 120 °C		4080 psi
@Strain 3.01 %,
Temperature 248 °F		ISO 11403-1/-2
 28.73 MPa
@Strain 3.40 %,
Temperature 120 °C		4167 psi
@Strain 3.40 %,
Temperature 248 °F		ISO 11403-1/-2
 28.98 MPa
@Strain 0.450 %,
Temperature 60.0 °C		4203 psi
@Strain 0.450 %,
Temperature 140 °F		ISO 11403-1/-2
 29.21 MPa
@Strain 3.79 %,
Temperature 120 °C		4237 psi
@Strain 3.79 %,
Temperature 248 °F		ISO 11403-1/-2
 29.63 MPa
@Strain 4.18 %,
Temperature 120 °C		4297 psi
@Strain 4.18 %,
Temperature 248 °F		ISO 11403-1/-2
 30.0 MPa
@Strain 1.15 %,
Temperature 90.0 °C		4350 psi
@Strain 1.15 %,
Temperature 194 °F		ISO 11403-1/-2
 30.01 MPa
@Strain 4.57 %,
Temperature 120 °C		4353 psi
@Strain 4.57 %,
Temperature 248 °F		ISO 11403-1/-2
 30.33 MPa
@Strain 4.98 %,
Temperature 120 °C		4399 psi
@Strain 4.98 %,
Temperature 248 °F		ISO 11403-1/-2
 30.61 MPa
@Strain 5.36 %,
Temperature 120 °C		4440 psi
@Strain 5.36 %,
Temperature 248 °F		ISO 11403-1/-2
 30.74 MPa
@Strain 0.310 %,
Temperature 0.000 °C		4458 psi
@Strain 0.310 %,
Temperature 32.0 °F		ISO 11403-1/-2
 30.87 MPa
@Strain 5.78 %,
Temperature 120 °C		4477 psi
@Strain 5.78 %,
Temperature 248 °F		ISO 11403-1/-2
 30.96 MPa
@Strain 7.49 %,
Temperature 120 °C		4490 psi
@Strain 7.49 %,
Temperature 248 °F		ISO 11403-1/-2
 31.09 MPa
@Strain 6.20 %,
Temperature 120 °C		4509 psi
@Strain 6.20 %,
Temperature 248 °F		ISO 11403-1/-2
 31.27 MPa
@Strain 6.61 %,
Temperature 120 °C		4535 psi
@Strain 6.61 %,
Temperature 248 °F		ISO 11403-1/-2
 31.41 MPa
@Strain 7.03 %,
Temperature 120 °C		4556 psi
@Strain 7.03 %,
Temperature 248 °F		ISO 11403-1/-2
 31.7 MPa
@Strain 0.360 %,
Temperature 40.0 °C		4600 psi
@Strain 0.360 %,
Temperature 104 °F		ISO 11403-1/-2
 32.66 MPa
@Strain 0.300 %,
Temperature -20.0 °C		4737 psi
@Strain 0.300 %,
Temperature -4.00 °F		ISO 11403-1/-2
 32.74 MPa
@Strain 1.40 %,
Temperature 90.0 °C		4749 psi
@Strain 1.40 %,
Temperature 194 °F		ISO 11403-1/-2
 34.79 MPa
@Strain 0.590 %,
Temperature 60.0 °C		5046 psi
@Strain 0.590 %,
Temperature 140 °F		ISO 11403-1/-2
 34.88 MPa
@Strain 1.66 %,
Temperature 90.0 °C		5059 psi
@Strain 1.66 %,
Temperature 194 °F		ISO 11403-1/-2
 35.35 MPa
@Strain 0.310 %,
Temperature -40.0 °C		5127 psi
@Strain 0.310 %,
Temperature -40.0 °F		ISO 11403-1/-2
 35.9 MPa
@Strain 0.350 %,
Temperature 23.0 °C		5210 psi
@Strain 0.350 %,
Temperature 73.4 °F		ISO 11403-1/-2
 36.55 MPa
@Strain 1.93 %,
Temperature 90.0 °C		5301 psi
@Strain 1.93 %,
Temperature 194 °F		ISO 11403-1/-2
 37.79 MPa
@Strain 2.20 %,
Temperature 90.0 °C		5481 psi
@Strain 2.20 %,
Temperature 194 °F		ISO 11403-1/-2
 38.45 MPa
@Strain 0.470 %,
Temperature 40.0 °C		5577 psi
@Strain 0.470 %,
Temperature 104 °F		ISO 11403-1/-2
 38.74 MPa
@Strain 2.48 %,
Temperature 90.0 °C		5619 psi
@Strain 2.48 %,
Temperature 194 °F		ISO 11403-1/-2
 39.45 MPa
@Strain 2.78 %,
Temperature 90.0 °C		5722 psi
@Strain 2.78 %,
Temperature 194 °F		ISO 11403-1/-2
 39.95 MPa
@Strain 3.08 %,
Temperature 90.0 °C		5794 psi
@Strain 3.08 %,
Temperature 194 °F		ISO 11403-1/-2
 40.33 MPa
@Strain 3.39 %,
Temperature 90.0 °C		5849 psi
@Strain 3.39 %,
Temperature 194 °F		ISO 11403-1/-2
 40.33 MPa
@Strain 5.44 %,
Temperature 90.0 °C		5849 psi
@Strain 5.44 %,
Temperature 194 °F		ISO 11403-1/-2
 40.61 MPa
@Strain 3.71 %,
Temperature 90.0 °C		5890 psi
@Strain 3.71 %,
Temperature 194 °F		ISO 11403-1/-2
 40.81 MPa
@Strain 4.04 %,
Temperature 90.0 °C		5919 psi
@Strain 4.04 %,
Temperature 194 °F		ISO 11403-1/-2
 40.93 MPa
@Strain 4.38 %,
Temperature 90.0 °C		5936 psi
@Strain 4.38 %,
Temperature 194 °F		ISO 11403-1/-2
 41.01 MPa
@Strain 4.73 %,
Temperature 90.0 °C		5948 psi
@Strain 4.73 %,
Temperature 194 °F		ISO 11403-1/-2
 41.02 MPa
@Strain 5.08 %,
Temperature 90.0 °C		5949 psi
@Strain 5.08 %,
Temperature 194 °F		ISO 11403-1/-2
 42.64 MPa
@Strain 0.440 %,
Temperature 0.000 °C		6184 psi
@Strain 0.440 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.29 MPa
@Strain 0.850 %,
Temperature 60.0 °C		6279 psi
@Strain 0.850 %,
Temperature 140 °F		ISO 11403-1/-2
 43.76 MPa
@Strain 0.560 %,
Temperature 40.0 °C		6347 psi
@Strain 0.560 %,
Temperature 104 °F		ISO 11403-1/-2
 45.1 MPa
@Strain 0.480 %,
Temperature 23.0 °C		6540 psi
@Strain 0.480 %,
Temperature 73.4 °F		ISO 11403-1/-2
 45.65 MPa
@Strain 0.430 %,
Temperature -20.0 °C		6621 psi
@Strain 0.430 %,
Temperature -4.00 °F		ISO 11403-1/-2
 46.77 MPa
@Strain 0.990 %,
Temperature 60.0 °C		6783 psi
@Strain 0.990 %,
Temperature 140 °F		ISO 11403-1/-2
 48.02 MPa
@Strain 0.420 %,
Temperature -40.0 °C		6965 psi
@Strain 0.420 %,
Temperature -40.0 °F		ISO 11403-1/-2
 48.38 MPa
@Strain 0.660 %,
Temperature 40.0 °C		7017 psi
@Strain 0.660 %,
Temperature 104 °F		ISO 11403-1/-2
 49.48 MPa
@Strain 1.14 %,
Temperature 60.0 °C		7176 psi
@Strain 1.14 %,
Temperature 140 °F		ISO 11403-1/-2
 51.47 MPa
@Strain 0.550 %,
Temperature 0.000 °C		7465 psi
@Strain 0.550 %,
Temperature 32.0 °F		ISO 11403-1/-2
 51.54 MPa
@Strain 0.580 %,
Temperature 23.0 °C		7475 psi
@Strain 0.580 %,
Temperature 73.4 °F		ISO 11403-1/-2
 52.04 MPa
@Strain 1.30 %,
Temperature 60.0 °C		7548 psi
@Strain 1.30 %,
Temperature 140 °F		ISO 11403-1/-2
 52.44 MPa
@Strain 0.770 %,
Temperature 40.0 °C		7606 psi
@Strain 0.770 %,
Temperature 104 °F		ISO 11403-1/-2
 54.16 MPa
@Strain 1.48 %,
Temperature 60.0 °C		7855 psi
@Strain 1.48 %,
Temperature 140 °F		ISO 11403-1/-2
 55.43 MPa
@Strain 0.530 %,
Temperature -20.0 °C		8039 psi
@Strain 0.530 %,
Temperature -4.00 °F		ISO 11403-1/-2
 55.94 MPa
@Strain 1.67 %,
Temperature 60.0 °C		8113 psi
@Strain 1.67 %,
Temperature 140 °F		ISO 11403-1/-2
 56.2 MPa
@Strain 0.880 %,
Temperature 40.0 °C		8150 psi
@Strain 0.880 %,
Temperature 104 °F		ISO 11403-1/-2
 56.58 MPa
@Strain 0.490 %,
Temperature -40.0 °C		8206 psi
@Strain 0.490 %,
Temperature -40.0 °F		ISO 11403-1/-2
 57.16 MPa
@Strain 0.700 %,
Temperature 23.0 °C		8290 psi
@Strain 0.700 %,
Temperature 73.4 °F		ISO 11403-1/-2
 57.32 MPa
@Strain 1.88 %,
Temperature 60.0 °C		8314 psi
@Strain 1.88 %,
Temperature 140 °F		ISO 11403-1/-2
 58.2 MPa
@Strain 3.26 %,
Temperature 60.0 °C		8440 psi
@Strain 3.26 %,
Temperature 140 °F		ISO 11403-1/-2
 58.3 MPa
@Strain 2.10 %,
Temperature 60.0 °C		8460 psi
@Strain 2.10 %,
Temperature 140 °F		ISO 11403-1/-2
 58.42 MPa
@Strain 0.660 %,
Temperature 0.000 °C		8473 psi
@Strain 0.660 %,
Temperature 32.0 °F		ISO 11403-1/-2
 58.86 MPa
@Strain 2.93 %,
Temperature 60.0 °C		8537 psi
@Strain 2.93 %,
Temperature 140 °F		ISO 11403-1/-2
 58.87 MPa
@Strain 2.36 %,
Temperature 60.0 °C		8538 psi
@Strain 2.36 %,
Temperature 140 °F		ISO 11403-1/-2
 59.04 MPa
@Strain 2.62 %,
Temperature 60.0 °C		8563 psi
@Strain 2.62 %,
Temperature 140 °F		ISO 11403-1/-2
 59.75 MPa
@Strain 1.01 %,
Temperature 40.0 °C		8666 psi
@Strain 1.01 %,
Temperature 104 °F		ISO 11403-1/-2
 62.03 MPa
@Strain 0.820 %,
Temperature 23.0 °C		8997 psi
@Strain 0.820 %,
Temperature 73.4 °F		ISO 11403-1/-2
 62.97 MPa
@Strain 1.15 %,
Temperature 40.0 °C		9133 psi
@Strain 1.15 %,
Temperature 104 °F		ISO 11403-1/-2
 63.19 MPa
@Strain 0.620 %,
Temperature -20.0 °C		9165 psi
@Strain 0.620 %,
Temperature -4.00 °F		ISO 11403-1/-2
 64.57 MPa
@Strain 0.570 %,
Temperature -40.0 °C		9365 psi
@Strain 0.570 %,
Temperature -40.0 °F		ISO 11403-1/-2
 64.65 MPa
@Strain 0.760 %,
Temperature 0.000 °C		9377 psi
@Strain 0.760 %,
Temperature 32.0 °F		ISO 11403-1/-2
 65.68 MPa
@Strain 1.31 %,
Temperature 40.0 °C		9526 psi
@Strain 1.31 %,
Temperature 104 °F		ISO 11403-1/-2
 65.96 MPa
@Strain 0.930 %,
Temperature 23.0 °C		9567 psi
@Strain 0.930 %,
Temperature 73.4 °F		ISO 11403-1/-2
 68.02 MPa
@Strain 1.48 %,
Temperature 40.0 °C		9865 psi
@Strain 1.48 %,
Temperature 104 °F		ISO 11403-1/-2
 69.71 MPa
@Strain 1.06 %,
Temperature 23.0 °C		10110 psi
@Strain 1.06 %,
Temperature 73.4 °F		ISO 11403-1/-2
 69.93 MPa
@Strain 1.66 %,
Temperature 40.0 °C		10140 psi
@Strain 1.66 %,
Temperature 104 °F		ISO 11403-1/-2
 69.98 MPa
@Strain 0.710 %,
Temperature -20.0 °C		10150 psi
@Strain 0.710 %,
Temperature -4.00 °F		ISO 11403-1/-2
 70.05 MPa
@Strain 0.870 %,
Temperature 0.000 °C		10160 psi
@Strain 0.870 %,
Temperature 32.0 °F		ISO 11403-1/-2
 71.32 MPa
@Strain 1.86 %,
Temperature 40.0 °C		10340 psi
@Strain 1.86 %,
Temperature 104 °F		ISO 11403-1/-2
 71.55 MPa
@Strain 0.640 %,
Temperature -40.0 °C		10380 psi
@Strain 0.640 %,
Temperature -40.0 °F		ISO 11403-1/-2
 71.79 MPa
@Strain 2.36 %,
Temperature 40.0 °C		10410 psi
@Strain 2.36 %,
Temperature 104 °F		ISO 11403-1/-2
 72.07 MPa
@Strain 2.09 %,
Temperature 40.0 °C		10450 psi
@Strain 2.09 %,
Temperature 104 °F		ISO 11403-1/-2
 73.06 MPa
@Strain 1.19 %,
Temperature 23.0 °C		10600 psi
@Strain 1.19 %,
Temperature 73.4 °F		ISO 11403-1/-2
 75.08 MPa
@Strain 0.990 %,
Temperature 0.000 °C		10890 psi
@Strain 0.990 %,
Temperature 32.0 °F		ISO 11403-1/-2
 76.11 MPa
@Strain 1.35 %,
Temperature 23.0 °C		11040 psi
@Strain 1.35 %,
Temperature 73.4 °F		ISO 11403-1/-2
 76.17 MPa
@Strain 0.800 %,
Temperature -20.0 °C		11050 psi
@Strain 0.800 %,
Temperature -4.00 °F		ISO 11403-1/-2
 78.37 MPa
@Strain 0.720 %,
Temperature -40.0 °C		11370 psi
@Strain 0.720 %,
Temperature -40.0 °F		ISO 11403-1/-2
 78.79 MPa
@Strain 1.51 %,
Temperature 23.0 °C		11430 psi
@Strain 1.51 %,
Temperature 73.4 °F		ISO 11403-1/-2
 79.53 MPa
@Strain 1.11 %,
Temperature 0.000 °C		11530 psi
@Strain 1.11 %,
Temperature 32.0 °F		ISO 11403-1/-2
 80.98 MPa
@Strain 1.67 %,
Temperature 23.0 °C		11750 psi
@Strain 1.67 %,
Temperature 73.4 °F		ISO 11403-1/-2
 82.02 MPa
@Strain 0.900 %,
Temperature -20.0 °C		11900 psi
@Strain 0.900 %,
Temperature -4.00 °F		ISO 11403-1/-2
 82.83 MPa
@Strain 1.85 %,
Temperature 23.0 °C		12010 psi
@Strain 1.85 %,
Temperature 73.4 °F		ISO 11403-1/-2
 83.85 MPa
@Strain 1.25 %,
Temperature 0.000 °C		12160 psi
@Strain 1.25 %,
Temperature 32.0 °F		ISO 11403-1/-2
 84.09 MPa
@Strain 2.06 %,
Temperature 23.0 °C		12200 psi
@Strain 2.06 %,
Temperature 73.4 °F		ISO 11403-1/-2
 84.17 MPa
@Strain 2.30 %,
Temperature 23.0 °C		12210 psi
@Strain 2.30 %,
Temperature 73.4 °F		ISO 11403-1/-2
 85.36 MPa
@Strain 0.800 %,
Temperature -40.0 °C		12380 psi
@Strain 0.800 %,
Temperature -40.0 °F		ISO 11403-1/-2
 87.48 MPa
@Strain 1.39 %,
Temperature 0.000 °C		12690 psi
@Strain 1.39 %,
Temperature 32.0 °F		ISO 11403-1/-2
 87.69 MPa
@Strain 1.01 %,
Temperature -20.0 °C		12720 psi
@Strain 1.01 %,
Temperature -4.00 °F		ISO 11403-1/-2
 90.77 MPa
@Strain 1.53 %,
Temperature 0.000 °C		13170 psi
@Strain 1.53 %,
Temperature 32.0 °F		ISO 11403-1/-2
 91.88 MPa
@Strain 0.880 %,
Temperature -40.0 °C		13330 psi
@Strain 0.880 %,
Temperature -40.0 °F		ISO 11403-1/-2
 92.92 MPa
@Strain 1.13 %,
Temperature -20.0 °C		13480 psi
@Strain 1.13 %,
Temperature -4.00 °F		ISO 11403-1/-2
 93.91 MPa
@Strain 1.68 %,
Temperature 0.000 °C		13620 psi
@Strain 1.68 %,
Temperature 32.0 °F		ISO 11403-1/-2
 96.62 MPa
@Strain 1.85 %,
Temperature 0.000 °C		14010 psi
@Strain 1.85 %,
Temperature 32.0 °F		ISO 11403-1/-2
 97.85 MPa
@Strain 1.24 %,
Temperature -20.0 °C		14190 psi
@Strain 1.24 %,
Temperature -4.00 °F		ISO 11403-1/-2
 98.36 MPa
@Strain 0.980 %,
Temperature -40.0 °C		14270 psi
@Strain 0.980 %,
Temperature -40.0 °F		ISO 11403-1/-2
 99.0 MPa
@Strain 2.04 %,
Temperature 0.000 °C		14400 psi
@Strain 2.04 %,
Temperature 32.0 °F		ISO 11403-1/-2
 100.7 MPa
@Strain 2.25 %,
Temperature 0.000 °C		14610 psi
@Strain 2.25 %,
Temperature 32.0 °F		ISO 11403-1/-2
 102.59 MPa
@Strain 1.38 %,
Temperature -20.0 °C		14879 psi
@Strain 1.38 %,
Temperature -4.00 °F		ISO 11403-1/-2
 104.51 MPa
@Strain 1.08 %,
Temperature -40.0 °C		15158 psi
@Strain 1.08 %,
Temperature -40.0 °F		ISO 11403-1/-2
 106.89 MPa
@Strain 1.53 %,
Temperature -20.0 °C		15503 psi
@Strain 1.53 %,
Temperature -4.00 °F		ISO 11403-1/-2
 110.53 MPa
@Strain 1.19 %,
Temperature -40.0 °C		16031 psi
@Strain 1.19 %,
Temperature -40.0 °F		ISO 11403-1/-2
 110.75 MPa
@Strain 1.68 %,
Temperature -20.0 °C		16063 psi
@Strain 1.68 %,
Temperature -4.00 °F		ISO 11403-1/-2
 114.21 MPa
@Strain 1.84 %,
Temperature -20.0 °C		16565 psi
@Strain 1.84 %,
Temperature -4.00 °F		ISO 11403-1/-2
 116.15 MPa
@Strain 1.30 %,
Temperature -40.0 °C		16846 psi
@Strain 1.30 %,
Temperature -40.0 °F		ISO 11403-1/-2
 117.13 MPa
@Strain 2.01 %,
Temperature -20.0 °C		16988 psi
@Strain 2.01 %,
Temperature -4.00 °F		ISO 11403-1/-2
 121.35 MPa
@Strain 1.43 %,
Temperature -40.0 °C		17600 psi
@Strain 1.43 %,
Temperature -40.0 °F		ISO 11403-1/-2
 126.13 MPa
@Strain 1.57 %,
Temperature -40.0 °C		18294 psi
@Strain 1.57 %,
Temperature -40.0 °F		ISO 11403-1/-2
 130.53 MPa
@Strain 1.71 %,
Temperature -40.0 °C		18932 psi
@Strain 1.71 %,
Temperature -40.0 °F		ISO 11403-1/-2
Elongation at Break 2.3 %
@Temperature 23.0 °C		2.3 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 9.70 GPa
@Temperature 23.0 °C		1410 ksi
@Temperature 73.4 °F		ISO 527
Charpy Impact Unnotched 2.40 J/cm²
@Temperature 23.0 °C		11.4 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
@Temperature 23.0 °C		2.38 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Processing PropertiesMetricEnglishComments
Melt Temperature 252 °C486 °F10°C/min; ISO 11357-1/-3
 285 °C545 °FOptimum
 280 - 300 °C536 - 572 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AppearanceBlack Color
FillerGlass fiber
FormsPellets
GenericPET
Material StatusPreliminary Data
Part Marking Code>PET-(MD+GF)35<ISO 11469
Processing MethodInjection Molding
Product CategoryGlass/Mineral Reinforced Resins
 Low Warp Resins
 UV Resistant/Weatherable Resins
Region Available - GlobalYes
Resin IdentificationPET-(MD+GF)35ISO 1043
RoHS ComplianceContact Manufacturer

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38898.html

免责声明: 本文 DuPont Performance Polymers Rynite® 935SUV BK593 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4