- 密度 [g/cm3]: 1.55
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 6.00
- 热变形温度 [℃]: 238.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Filler Content | 15 % | 15 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa @Temperature 23.0 °C | 14500 psi @Temperature 73.4 °F | ISO 527 | ||
| 125 MPa @Temperature -40.0 °C | 18100 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | 2.0 % @Temperature -40.0 °C | 2.0 % @Temperature -40.0 °F | ISO 527 | ||
| 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | ISO 527 | |||
| Tensile Modulus | 3.59 GPa @Temperature 150 °C | 521 ksi @Temperature 302 °F | ISO 527 | ||
| 6.135 GPa @Temperature 23.0 °C | 889.8 ksi @Temperature 73.4 °F | ISO 527 | |||
| 7.721 GPa @Temperature -40.0 °C | 1120 ksi @Temperature -40.0 °F | ISO 527 | |||
| Flexural Strength | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | ISO 178 | ||
| 180 MPa @Temperature -40.0 °C | 26100 psi @Temperature -40.0 °F | ISO 178 | |||
| Flexural Modulus | 6.00 GPa @Temperature 23.0 °C | 870 ksi @Temperature 73.4 °F | ISO 178 | ||
| 6.737 GPa @Temperature -40.0 °C | 977.1 ksi @Temperature -40.0 °F | ISO 178 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | ISO 180/1A | ||
| 5.50 kJ/m² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² @Temperature -40.0 °C | 8.57 ft-lb/in² @Temperature -40.0 °F | ISO 180/1U | ||
| 26.0 kJ/m² @Temperature 23.0 °C | 12.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature -40.0 °C | 9.52 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eU | ||
| 3.20 J/cm² @Temperature 23.0 °C | 15.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eA | ||
| 0.620 J/cm² @Temperature 23.0 °C | 2.95 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 175 - 250 V @Temperature 23.0 °C | 175 - 250 V @Temperature 73.4 °F | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 74.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 41.1 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | ||
| 95.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 52.8 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 125 µm/m-°C @Temperature 55.0 - 160 °C | 69.4 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 238 °C | 460 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 0.860 mm | 284 °F @Thickness 0.0339 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 140 °C @Thickness 0.860 mm | 284 °F @Thickness 0.0339 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 0.860 mm | 284 °F @Thickness 0.0339 in | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.860 mm | V-0 @Thickness 0.0339 in | IEC 60695-11-10 | ||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| V-0 @Thickness 0.860 mm | V-0 @Thickness 0.0339 in | UL94 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | IEC 60695-11-20 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | IEC 60695-11-10 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 254 °C | 489 °F | 10°C/min; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | Optimum | |||
| 270 - 290 °C | 518 - 554 °F | ||||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| 110 °C | 230 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Additive | Flame Retardant | ||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Dimensional Stability, Good | ||||
| Electrical Properties, Good | |||||
| Flame Retardant | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Glass Reinforced | |||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-GF15FR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Flame Retardant Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-GF15FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Appliances | ||||
| Electrical Parts | |||||
| Electrical/Electronic Applications | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||