- 密度 [g/cm3]: 1.57
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 162 MPa @Temperature 23.0 °C | 23500 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 10.5 GPa @Temperature 23.0 °C | 1520 ksi @Temperature 73.4 °F | ISO 527 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 242 °C | 468 °F | ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 257 °C | 495 °F | ISO 11357-1/-3 | ||
| 280 - 300 °C | 536 - 572 °F | ||||
| Mold Temperature | 130 - 140 °C | 266 - 284 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PET-GF30< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Food Contact Resins | ||||
| Glass Reinforced Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-GF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Food Applications, Non-specific | ||||