- 密度 [g/cm3]: 1.64
- 吸水率 [%]: 0.05
- 成型收缩率 [%]: 0.0017
- 缺口冲击强度: 0.69
- 弯曲模量 [MPa]: 2.10
- 硬度: 115.0
- 热变形温度 [℃]: 241.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | ASTM D792 | ||
| Density | 1.64 g/cc | 0.0592 lb/in³ | ISO 1183 | ||
| Filler Content | 40 % | 40 % | |||
| Water Absorption | 0.050 % @Temperature 23.0 °C | 0.050 % @Temperature 73.4 °F | 50%RH,23°C,24h; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0017 cm/cm @Thickness 1.57 mm | 0.0017 in/in @Thickness 0.0618 in | Flow | ||
| 0.0030 cm/cm @Thickness 3.20 mm | 0.0030 in/in @Thickness 0.126 in | Flow | |||
| 0.0055 cm/cm @Thickness 1.57 mm | 0.0055 in/in @Thickness 0.0618 in | Transverse | |||
| 0.0070 cm/cm @Thickness 3.20 mm | 0.0070 in/in @Thickness 0.126 in | Transverse | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Thickness 2.00 mm | 0.0070 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 75 | 75 | ASTM D785 | ||
| Hardness, Rockwell R | 115 | 115 | ASTM D785 | ||
| Tensile Strength at Break | 40.0 MPa @Temperature 150 °C | 5800 psi @Temperature 302 °F | ISO 527 | ||
| 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | ISO 527 | |||
| 160 MPa @Temperature -40.0 °C | 23200 psi @Temperature -40.0 °F | ISO 527 | |||
| Tensile Strength | 38.6 MPa @Temperature 150 °C | 5600 psi @Temperature 302 °F | ASTM D638 | ||
| 55.2 MPa @Temperature 90.0 °C | 8010 psi @Temperature 194 °F | ASTM D638 | |||
| 117 MPa @Temperature 23.0 °C | 17000 psi @Temperature 73.4 °F | ASTM D638 | |||
| 152 MPa @Temperature -40.0 °C | 22000 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | 1.6 % @Temperature -40.0 °C | 1.6 % @Temperature -40.0 °F | ASTM D638 | ||
| 1.7 % @Temperature -40.0 °C | 1.7 % @Temperature -40.0 °F | ISO 527 | |||
| 1.8 % @Temperature 23.0 °C | 1.8 % @Temperature 73.4 °F | ISO 527 | |||
| 1.9 % @Temperature 23.0 °C | 1.9 % @Temperature 73.4 °F | ASTM D638 | |||
| 5.5 % @Temperature 90.0 °C | 5.5 % @Temperature 194 °F | ASTM D638 | |||
| 5.5 % @Temperature 150 °C | 5.5 % @Temperature 302 °F | ISO 527 | |||
| 6.5 % @Temperature 150 °C | 6.5 % @Temperature 302 °F | ASTM D638 | |||
| Tensile Modulus | 3.19 GPa @Temperature 150 °C | 463 ksi @Temperature 302 °F | ASTM D638 | ||
| 3.284 GPa @Temperature 150 °C | 476.3 ksi @Temperature 302 °F | ISO 527 | |||
| 4.45 GPa @Temperature 90.0 °C | 645 ksi @Temperature 194 °F | ASTM D638 | |||
| 11.6 GPa @Temperature 23.0 °C | 1680 ksi @Temperature 73.4 °F | ASTM D638 | |||
| 12.5 GPa @Temperature 23.0 °C | 1810 ksi @Temperature 73.4 °F | ISO 527 | |||
| 13.9 GPa @Temperature -40.0 °C | 2020 ksi @Temperature -40.0 °F | ASTM D638 | |||
| Flexural Strength | 49.0 MPa @Temperature 150 °C | 7110 psi @Temperature 302 °F | ASTM D790 | ||
| 73.1 MPa @Temperature 90.0 °C | 10600 psi @Temperature 194 °F | ASTM D790 | |||
| 198 MPa @Temperature 23.0 °C | 28700 psi @Temperature 73.4 °F | ASTM D790 | |||
| 261 MPa @Temperature -40.0 °C | 37900 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.10 GPa @Temperature 150 °C | 305 ksi @Temperature 302 °F | ASTM D790 | ||
| 3.58 GPa @Temperature 90.0 °C | 519 ksi @Temperature 194 °F | ASTM D790 | |||
| 11.7 GPa @Temperature 23.0 °C | 1700 ksi @Temperature 73.4 °F | ASTM D790 | |||
| 12.951 GPa @Temperature 23.0 °C | 1878.4 ksi @Temperature 73.4 °F | ISO 178 | |||
| 13.2 GPa @Temperature -40.0 °C | 1910 ksi @Temperature -40.0 °F | ASTM D790 | |||
| 14.18 GPa @Temperature -40.0 °C | 2057 ksi @Temperature -40.0 °F | ISO 178 | |||
| Compressive Strength | 175 MPa @Temperature 23.0 °C | 25400 psi @Temperature 73.4 °F | ASTM D695 | ||
| Shear Strength | 60.7 MPa @Temperature 23.0 °C | 8800 psi @Temperature 73.4 °F | ASTM D732 | ||
| Izod Impact, Notched | 0.690 J/cm @Temperature -40.0 °C | 1.29 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.750 J/cm @Temperature 23.0 °C | 1.41 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 4.15 J/cm @Temperature -40.0 °C | 7.77 ft-lb/in @Temperature -40.0 °F | ASTM D4812 | ||
| 5.30 J/cm @Temperature 23.0 °C | 9.93 ft-lb/in @Temperature 73.4 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -40.0 °C | 3.33 ft-lb/in² @Temperature -40.0 °F | ISO 180/1A | ||
| 7.00 kJ/m² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 36.0 kJ/m² @Temperature 23.0 °C | 17.1 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | ||
| 39.0 kJ/m² @Temperature -40.0 °C | 18.6 ft-lb/in² @Temperature -40.0 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -40.0 °C | 16.7 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature 23.0 °C | 16.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | ASTM D257 | ||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | IEC 60093 | |||
| Surface Resistance | 1.00e+14 ohm @Temperature 23.0 °C | 1.00e+14 ohm @Temperature 73.4 °F | ASTM D257 | ||
| 1.00e+14 ohm @Temperature 23.0 °C | 1.00e+14 ohm @Temperature 73.4 °F | IEC 60093 | |||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | ||
| 3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 | |||
| 3.8 @Frequency 1000 Hz, Temperature 23.0 °C | 3.8 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D150 | |||
| 3.8 @Frequency 100 Hz, Temperature 23.0 °C | 3.8 @Frequency 100 Hz, Temperature 73.4 °F | IEC 60250 | |||
| Dielectric Strength | 10.5 kV/mm @Thickness 3.20 mm, Temperature 150 °C | 267 kV/in @Thickness 0.126 in, Temperature 302 °F | 500 V/s, in oil; Short Time; ASTM D149 | ||
| 14.0 kV/mm @Thickness 3.20 mm, Temperature 95.0 °C | 356 kV/in @Thickness 0.126 in, Temperature 203 °F | 500 V/s, in oil; Short Time; ASTM D149 | |||
| 15.0 kV/mm @Thickness 1.60 mm, Temperature 150 °C | 381 kV/in @Thickness 0.0630 in, Temperature 302 °F | 500 V/s, in oil; Short Time; ASTM D149 | |||
| 16.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 419 kV/in @Thickness 0.126 in, Temperature 73.4 °F | 500 V/s, in oil; Short Time; ASTM D149 | |||
| 19.0 kV/mm @Thickness 1.60 mm, Temperature 95.0 °C | 483 kV/in @Thickness 0.0630 in, Temperature 203 °F | 500 V/s, in oil; Short Time; ASTM D149 | |||
| 23.0 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C | 584 kV/in @Thickness 0.0630 in, Temperature 73.4 °F | 500 V/s, in oil; Short Time; ASTM D149 | |||
| Dissipation Factor | 0.0070 @Frequency 1000 Hz, Temperature 23.0 °C | 0.0070 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D150 | ||
| 0.0070 @Frequency 100 Hz, Temperature 23.0 °C | 0.0070 @Frequency 100 Hz, Temperature 73.4 °F | IEC 60250 | |||
| 0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | |||
| 0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| 500 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ASTM E 831 | |||
| 500 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 30.0 µin/in-°F @Temperature -40.0 - 73.4 °F | ASTM E 831 | ||
| 54.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 30.0 µin/in-°F @Temperature -40.0 - 73.4 °F | ISO 11359-1/-2 | |||
| 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | ASTM E 831 | |||
| 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 84.0 µm/m-°C @Temperature 55.0 - 160 °C | 46.7 µin/in-°F @Temperature 131 - 320 °F | ASTM E 831 | |||
| 84.0 µm/m-°C @Temperature 55.0 - 160 °C | 46.7 µin/in-°F @Temperature 131 - 320 °F | ISO 11359-1/-2 | |||
| Melting Point | 250 °C | 482 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 241 °C | 466 °F | ISO 75-1/-2 | ||
| 241 °C | 466 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | ASTM D648 | ||
| 220 °C | 428 °F | ISO 75-1/-2 | |||
| UL RTI, Electrical | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | Optimum | |||
| 280 - 300 °C | 536 - 572 °F | ||||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| 110 °C | 230 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Dimensional Stability, Good | ||||
| Electrical Properties, Good | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Warp Resistant | |||||
| Filler | Glass/Mica | ||||
| Forms | Pellets | ||||
| Generic | PET | ||||
| Heat Stabilized | Yes | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PET-(GF+MD)40< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass/Mineral Reinforced Resins | ||||
| Low Warp Resins | |||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-(GF+MD)40 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Ultrasonic Weldable | Yes | ||||
| Uses | Automotive Applications | ||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||