- 密度 [g/cm3]: 1.43
- 缺口冲击强度: 5.0
- 弯曲模量 [MPa]: 5.60
- 热变形温度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ISO 1183 | ||
| Filler Content | 15 % | 15 % | |||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 97.0 MPa @Temperature 23.0 °C | 14100 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.4 % @Temperature 23.0 °C | 2.4 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 6.20 GPa @Temperature 23.0 °C | 899 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Modulus | 5.60 GPa @Temperature 23.0 °C | 812 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | ISO 180/1A | ||
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Charpy Impact Unnotched | 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eA | ||
| 0.500 J/cm² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| UL RTI, Mechanical without Impact | 75.0 °C @Thickness 0.750 mm | 167 °F @Thickness 0.0295 in | UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | UL94 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 °C | 482 °F | 10°C/min; ISO 11357-1/-3 | ||
| 280 °C | 536 °F | Optimum | |||
| 270 - 290 °C | 518 - 554 °F | ||||
| Mold Temperature | 135 °C | 275 °F | optimum | ||
| 130 - 140 °C | 266 - 284 °F | ||||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Filler | Glass Reinforced | ||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-GF15< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Product Category | Color Stable Resins | ||||
| Glass Reinforced Resins | |||||
| Resin Identification | PET-GF15 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||