- 密度 [g/cm3]: 1.56
- 缺口冲击强度: 8.5
- 弯曲模量 [MPa]: 3.00
- 热变形温度 [℃]: 244.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | ||
| Filler Content | 30 % | 30 % | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; ISO 294-4, Similar | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; ISO 294-4, Similar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa @Temperature 23.0 °C | 21800 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 10.2 GPa @Temperature 23.0 °C | 1480 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Strength | 210 MPa @Temperature 23.0 °C | 30500 psi @Temperature 73.4 °F | ISO 178 | ||
| Flexural Modulus | 3.00 GPa @Temperature 150 °C | 435 ksi @Temperature 302 °F | ISO 178 | ||
| 5.165 GPa @Temperature 90.0 °C | 749.1 ksi @Temperature 194 °F | ISO 178 | |||
| 8.94 GPa @Temperature 23.0 °C | 1300 ksi @Temperature 73.4 °F | ISO 178 | |||
| 10.367 GPa @Temperature -40.0 °C | 1503.6 ksi @Temperature -40.0 °F | ISO 178 | |||
| Izod Impact, Notched (ISO) | 8.50 kJ/m² @Temperature -40.0 °C | 4.04 ft-lb/in² @Temperature -40.0 °F | ISO 180/1A | ||
| 9.50 kJ/m² @Temperature 23.0 °C | 4.52 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² @Temperature -40.0 °C | 16.7 ft-lb/in² @Temperature -40.0 °F | ISO 180/1U | ||
| 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -40.0 °C | 21.4 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eU | ||
| 5.20 J/cm² @Temperature 23.0 °C | 24.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -40.0 °C | 3.81 ft-lb/in² @Temperature -40.0 °F | ISO 179/1eA | ||
| 0.850 J/cm² @Temperature -30.0 °C | 4.04 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| 0.950 J/cm² @Temperature 23.0 °C | 4.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C | 559 kV/in @Thickness 0.0787 in, Temperature 73.4 °F | 2000 V/s, in oil; IEC 60243-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 244 °C | 471 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B | ||
| 140 °C @Thickness 0.810 mm | 284 °F @Thickness 0.0319 in | UL 746B | |||
| 140 °C @Thickness 6.00 mm | 284 °F @Thickness 0.236 in | UL 746B | |||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 2.00 mm | 284 °F @Thickness 0.0787 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 140 °C | 284 °F | UL 746B | ||
| 140 °C @Thickness 0.810 mm | 284 °F @Thickness 0.0319 in | UL 746B | |||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 2.00 mm | 284 °F @Thickness 0.0787 in | UL 746B | |||
| 140 °C @Thickness 6.00 mm | 284 °F @Thickness 0.236 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B | ||
| 140 °C @Thickness 2.00 mm | 284 °F @Thickness 0.0787 in | UL 746B | |||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 0.810 mm | 284 °F @Thickness 0.0319 in | UL 746B | |||
| 140 °C @Thickness 6.00 mm | 284 °F @Thickness 0.236 in | UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| HB @Thickness 2.00 mm | HB @Thickness 0.0787 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | IEC 60695-11-10 | |||
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | UL94 | |||
| HB @Thickness 2.00 mm | HB @Thickness 0.0787 in | UL94 | |||
| Glow Wire Test | 800 °C @Thickness 2.00 mm | 1470 °F @Thickness 0.0787 in | IEC 60695-2-12 | ||
| 825 °C @Thickness 2.00 mm | 1520 °F @Thickness 0.0787 in | Ignition; IEC 60695-2-13 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 285 °C | 545 °F | Optimum | ||
| 280 - 300 °C | 536 - 572 °F | ||||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| 110 °C | 230 °F | optimum | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Appearance | Black Color | ||||
| Drying Recommended | Yes | ||||
| Features | Electrical Properties, Good | ||||
| Fatigue Resistance | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Forms | Pellets | ||||
| Pellets | |||||
| Generic | PET | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Glass Reinforced Resins | ||||
| Region Available - Global | Yes | ||||
| Resin Identification | PET-GF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Automotive Applications | ||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Phenolic Replacement | |||||
| Structural Parts | |||||