- 吸水率 [%]: 0.06
- 成型收缩率 [%]: 0.0013
- 缺口冲击强度: 0.85
- 弯曲模量 [MPa]: 2.80
- 硬度: 120.0
- 热变形温度 [℃]: 251.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 | ||
| Filler Content | 30 % | 30 % | |||
| Water Absorption | 0.060 % @Temperature 23.0 °C | 0.060 % @Temperature 73.4 °F | 50%RH,23°C,24h; ASTM D570 | ||
| 0.060 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.060 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.0013 cm/cm @Thickness 1.57 mm | 0.0013 in/in @Thickness 0.0618 in | Flow; ASTM D955 | ||
| 0.0015 cm/cm @Thickness 3.20 mm | 0.0015 in/in @Thickness 0.126 in | Flow; ASTM D955 | |||
| 0.0060 cm/cm @Thickness 1.57 mm | 0.0060 in/in @Thickness 0.0618 in | Transverse; ASTM D955 | |||
| 0.0070 cm/cm @Thickness 3.20 mm | 0.0070 in/in @Thickness 0.126 in | Transverse; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 100 | 100 | ASTM D785 | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength at Break | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | ISO 527 | ||
| Tensile Strength | 68.0 MPa @Temperature 150 °C | 9860 psi @Temperature 302 °F | ASTM D638 | ||
| 107 MPa @Temperature 93.0 °C | 15500 psi @Temperature 199 °F | ASTM D638 | |||
| 169 MPa @Temperature 23.0 °C | 24500 psi @Temperature 73.4 °F | ASTM D638 | |||
| 193 MPa @Temperature -40.0 °C | 28000 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | 2.1 % @Temperature -40.0 °C | 2.1 % @Temperature -40.0 °F | ASTM D638 | ||
| 2.3 % @Temperature 23.0 °C | 2.3 % @Temperature 73.4 °F | ASTM D638 | |||
| 2.3 % @Temperature 23.0 °C | 2.3 % @Temperature 73.4 °F | ISO 527 | |||
| 3.6 % @Temperature 93.0 °C | 3.6 % @Temperature 199 °F | ASTM D638 | |||
| 6.5 % @Temperature 150 °C | 6.5 % @Temperature 302 °F | ASTM D638 | |||
| Tensile Modulus | 4.38 GPa @Temperature 150 °C | 635 ksi @Temperature 302 °F | ASTM D638 | ||
| 7.59 GPa @Temperature 93.0 °C | 1100 ksi @Temperature 199 °F | ASTM D638 | |||
| 10.7 GPa @Temperature 23.0 °C | 1550 ksi @Temperature 73.4 °F | ASTM D638 | |||
| 10.7 GPa @Temperature 23.0 °C | 1550 ksi @Temperature 73.4 °F | ISO 527 | |||
| 11.2 GPa @Temperature -40.0 °C | 1620 ksi @Temperature -40.0 °F | ASTM D638 | |||
| Flexural Strength | 82.3 MPa @Temperature 150 °C | 11900 psi @Temperature 302 °F | ASTM D790 | ||
| 98.6 MPa @Temperature 93.0 °C | 14300 psi @Temperature 199 °F | ASTM D790 | |||
| 240 MPa @Temperature 23.0 °C | 34800 psi @Temperature 73.4 °F | ASTM D790 | |||
| 276 MPa @Temperature -40.0 °C | 40000 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.80 GPa @Temperature 150 °C | 406 ksi @Temperature 302 °F | ASTM D790 | ||
| 3.99 GPa @Temperature 93.0 °C | 579 ksi @Temperature 199 °F | ASTM D790 | |||
| 8.96 GPa @Temperature 23.0 °C | 1300 ksi @Temperature 73.4 °F | ASTM D790 | |||
| 9.66 GPa @Temperature -40.0 °C | 1400 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Compressive Strength | 241 MPa @Temperature 23.0 °C | 35000 psi @Temperature 73.4 °F | ASTM D695 | ||
| Shear Strength | 74.5 MPa @Temperature 23.0 °C | 10800 psi @Temperature 73.4 °F | ASTM D732 | ||
| Izod Impact, Notched | 0.850 J/cm @Temperature -40.0 °C | 1.59 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 6.40 J/cm @Temperature -40.0 °C | 12.0 ft-lb/in @Temperature -40.0 °F | ASTM D4812 | ||
| 6.95 J/cm @Temperature 23.0 °C | 13.0 ft-lb/in @Temperature 73.4 °F | ASTM D4812 | |||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | ASTM D257 | ||
| 1.00e+17 ohm-cm @Temperature 23.0 °C | 1.00e+17 ohm-cm @Temperature 73.4 °F | IEC 60093 | |||
| Surface Resistance | 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | ASTM D257 | ||
| 1.00e+13 ohm @Temperature 23.0 °C | 1.00e+13 ohm @Temperature 73.4 °F | IEC 60093 | |||
| Dielectric Constant | 4.1 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 4.1 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | ||
| 4.2 @Frequency 1000 Hz, Temperature 23.0 °C | 4.2 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D150 | |||
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm, Temperature 200 °C | 381 kV/in @Thickness 0.126 in, Temperature 392 °F | Short Time; ASTM D149 | ||
| 19.0 kV/mm @Thickness 3.20 mm, Temperature 95.0 °C | 483 kV/in @Thickness 0.126 in, Temperature 203 °F | Short Time; ASTM D149 | |||
| 19.0 kV/mm @Thickness 3.20 mm, Temperature 150 °C | 483 kV/in @Thickness 0.126 in, Temperature 302 °F | Short Time; ASTM D149 | |||
| 21.5 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C | 546 kV/in @Thickness 0.126 in, Temperature 73.4 °F | Short Time; ASTM D149 | |||
| 21.5 kV/mm @Thickness 1.57 mm, Temperature 200 °C | 546 kV/in @Thickness 0.0618 in, Temperature 392 °F | Short Time; ASTM D149 | |||
| 23.0 kV/mm @Thickness 1.57 mm, Temperature 95.0 °C | 584 kV/in @Thickness 0.0618 in, Temperature 203 °F | Short Time; ASTM D149 | |||
| 23.5 kV/mm @Thickness 1.57 mm, Temperature 150 °C | 597 kV/in @Thickness 0.0618 in, Temperature 302 °F | Short Time; ASTM D149 | |||
| 25.0 kV/mm @Thickness 1.57 mm, Temperature 23.0 °C | 635 kV/in @Thickness 0.0618 in, Temperature 73.4 °F | Short Time; ASTM D149 | |||
| Dissipation Factor | 0.0040 @Frequency 1000 Hz, Temperature 23.0 °C | 0.0040 @Frequency 1000 Hz, Temperature 73.4 °F | ASTM D150 | ||
| 0.014 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.014 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | ASTM D150 | |||
| Comparative Tracking Index | 200 V @Thickness 3.00 mm, Temperature 23.0 °C | 200 V @Thickness 0.118 in, Temperature 73.4 °F | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | ASTM E 228 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | ASTM E 228 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | ASTM E 228 | |||
| CTE, linear, Transverse to Flow | 56.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 31.1 µin/in-°F @Temperature -40.0 - 73.4 °F | ASTM E 228 | ||
| 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | ASTM E 228 | |||
| 60.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 33.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1/-2 | |||
| 90.0 µm/m-°C @Temperature 55.0 - 160 °C | 50.0 µin/in-°F @Temperature 131 - 320 °F | ASTM E 228 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 251 °C | 484 °F | ISO 75-1/-2 | ||
| 251 °C | 484 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | ISO 75-1/-2 | ||
| 233 °C | 451 °F | ASTM D648 | |||
| UL RTI, Electrical | 140 °C @Thickness 0.850 mm | 284 °F @Thickness 0.0335 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 140 °C @Thickness 0.850 mm | 284 °F @Thickness 0.0335 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 0.850 mm | 284 °F @Thickness 0.0335 in | UL 746B | ||
| 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL 746B | |||
| 140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.850 mm | HB @Thickness 0.0335 in | IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL94 | |||
| HB @Thickness 0.850 mm | HB @Thickness 0.0335 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |||
| Mold Temperature | >= 95.0 °C | >= 203 °F | |||
| Drying Temperature | 120 °C | 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Descriptive Properties | |||||
| Additive | Impact Modifier | ||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes | ||||
| Features | Flow, Good | ||||
| Impact Modified | |||||
| Impact Resistance, Good | |||||
| Stiffness, Good | |||||
| Strength, Good | |||||
| Thermal Aging Resistance, Good | |||||
| Filler | Glass fiber reinforcement | ||||
| Generic | PET | ||||
| Heat Stabilized | Yes | ||||
| Material Status | Current | ||||
| Part Marking Code | >PET-GF30< | ISO 11469 | |||
| Polymer Family | Polyester | ||||
| Polymer Type | PET | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Encapsulation Resins | ||||
| Glass Reinforced Resins | |||||
| Resin Identification | PET-GF30 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Ultrasonic Weldable | Yes | ||||
| Uses | Electrical/Electronic Applications | ||||
| Housings | |||||
| Parts, Thin-walled | |||||