DuPont Performance Polymers Rynite® 408 NC010 PET

DuPont Performance Polymers Rynite® 408 NC010 PET 物性表: DuPont Performance Polymers Rynite® 408 NC010 PET物性表及特性介绍,DuPont Performance Polymers Rynite® 408 NC010 PET注塑参数详情,如需DuPont Performance Polymers Rynite® 408 NC010 PET下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.49
  • 吸水率 [%]: 0.06
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 1.01
  • 弯曲模量 [MPa]: 2.25
  • 硬度: 115.0
  • 热变形温度 [℃]: 237.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.51 g/cc1.51 g/ccASTM D792
Density 1.49 g/cc0.0538 lb/in³ISO 1183
Filler Content 30 %30 %
Water Absorption 0.060 %
@Temperature 23.0 °C		0.060 %
@Temperature 73.4 °F		50%RH,23°C,24h; ASTM D570
Viscosity  110000 cP
@Shear Rate 3090 1/s,
Temperature 305 °C		110000 cP
@Shear Rate 3090 1/s,
Temperature 581 °F		ISO 11443
 138000 cP
@Shear Rate 3090 1/s,
Temperature 290 °C		138000 cP
@Shear Rate 3090 1/s,
Temperature 554 °F		ISO 11443
 157000 cP
@Shear Rate 1450 1/s,
Temperature 305 °C		157000 cP
@Shear Rate 1450 1/s,
Temperature 581 °F		ISO 11443
 172000 cP
@Shear Rate 3090 1/s,
Temperature 275 °C		172000 cP
@Shear Rate 3090 1/s,
Temperature 527 °F		ISO 11443
 215000 cP
@Shear Rate 1450 1/s,
Temperature 290 °C		215000 cP
@Shear Rate 1450 1/s,
Temperature 554 °F		ISO 11443
 218000 cP
@Shear Rate 681 1/s,
Temperature 305 °C		218000 cP
@Shear Rate 681 1/s,
Temperature 581 °F		ISO 11443
 260000 cP
@Shear Rate 1450 1/s,
Temperature 275 °C		260000 cP
@Shear Rate 1450 1/s,
Temperature 527 °F		ISO 11443
 318000 cP
@Shear Rate 681 1/s,
Temperature 290 °C		318000 cP
@Shear Rate 681 1/s,
Temperature 554 °F		ISO 11443
 322000 cP
@Shear Rate 316 1/s,
Temperature 305 °C		322000 cP
@Shear Rate 316 1/s,
Temperature 581 °F		ISO 11443
 386000 cP
@Shear Rate 681 1/s,
Temperature 275 °C		386000 cP
@Shear Rate 681 1/s,
Temperature 527 °F		ISO 11443
 454000 cP
@Shear Rate 316 1/s,
Temperature 290 °C		454000 cP
@Shear Rate 316 1/s,
Temperature 554 °F		ISO 11443
 463000 cP
@Shear Rate 146 1/s,
Temperature 305 °C		463000 cP
@Shear Rate 146 1/s,
Temperature 581 °F		ISO 11443
 560000 cP
@Shear Rate 316 1/s,
Temperature 275 °C		560000 cP
@Shear Rate 316 1/s,
Temperature 527 °F		ISO 11443
 655000 cP
@Shear Rate 146 1/s,
Temperature 290 °C		655000 cP
@Shear Rate 146 1/s,
Temperature 554 °F		ISO 11443
 663000 cP
@Shear Rate 73.0 1/s,
Temperature 305 °C		663000 cP
@Shear Rate 73.0 1/s,
Temperature 581 °F		ISO 11443
 810000 cP
@Shear Rate 146 1/s,
Temperature 275 °C		810000 cP
@Shear Rate 146 1/s,
Temperature 527 °F		ISO 11443
 935000 cP
@Shear Rate 73.0 1/s,
Temperature 290 °C		935000 cP
@Shear Rate 73.0 1/s,
Temperature 554 °F		ISO 11443
 1.00e+6 cP
@Shear Rate 36.0 1/s,
Temperature 305 °C		1.00e+6 cP
@Shear Rate 36.0 1/s,
Temperature 581 °F		ISO 11443
 1.17e+6 cP
@Shear Rate 73.0 1/s,
Temperature 275 °C		1.17e+6 cP
@Shear Rate 73.0 1/s,
Temperature 527 °F		ISO 11443
 1.29e+6 cP
@Shear Rate 36.0 1/s,
Temperature 290 °C		1.29e+6 cP
@Shear Rate 36.0 1/s,
Temperature 554 °F		ISO 11443
 1.62e+6 cP
@Shear Rate 36.0 1/s,
Temperature 275 °C		1.62e+6 cP
@Shear Rate 36.0 1/s,
Temperature 527 °F		ISO 11443
 1.73e+6 cP
@Shear Rate 12.0 1/s,
Temperature 305 °C		1.73e+6 cP
@Shear Rate 12.0 1/s,
Temperature 581 °F		ISO 11443
 1.97e+6 cP
@Shear Rate 7.30 1/s,
Temperature 305 °C		1.97e+6 cP
@Shear Rate 7.30 1/s,
Temperature 581 °F		ISO 11443
 2.55e+6 cP
@Shear Rate 12.0 1/s,
Temperature 290 °C		2.55e+6 cP
@Shear Rate 12.0 1/s,
Temperature 554 °F		ISO 11443
 2.96e+6 cP
@Shear Rate 12.0 1/s,
Temperature 275 °C		2.96e+6 cP
@Shear Rate 12.0 1/s,
Temperature 527 °F		ISO 11443
 3.33e+6 cP
@Shear Rate 7.30 1/s,
Temperature 290 °C		3.33e+6 cP
@Shear Rate 7.30 1/s,
Temperature 554 °F		ISO 11443
 4.11e+6 cP
@Shear Rate 7.30 1/s,
Temperature 275 °C		4.11e+6 cP
@Shear Rate 7.30 1/s,
Temperature 527 °F		ISO 11443
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 3.20 mm		0.0020 in/in
@Thickness 0.126 in		Flow
 0.0021 cm/cm
@Thickness 1.60 mm		0.0021 in/in
@Thickness 0.0630 in		Flow
 0.0063 cm/cm
@Thickness 1.60 mm		0.0063 in/in
@Thickness 0.0630 in		Transverse
 0.0075 cm/cm
@Thickness 3.20 mm		0.0075 in/in
@Thickness 0.126 in		Transverse
Linear Mold Shrinkage, Flow 0.0035 cm/cm0.0035 in/inParallel; Annealed; ISO 294-4
 0.0025 cm/cm
@Thickness 2.00 mm		0.0025 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0105 cm/cm0.0105 in/inNormal; Annealed; ISO 294-4
 0.0085 cm/cm
@Thickness 2.00 mm		0.0085 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 5.5 g/10 min
@Load 5.00 kg,
Temperature 280 °C		5.5 g/10 min
@Load 11.0 lb,
Temperature 536 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Hardness, Rockwell M 7070ASTM D785
 7070ISO 2039/2
Hardness, Rockwell R 115115ASTM D785
 115115ISO 2039/2
Tensile Strength at Break 125 MPa
@Temperature 23.0 °C		18100 psi
@Temperature 73.4 °F		ISO 527
Tensile Strength  55.2 MPa
@Temperature 150 °C		8010 psi
@Temperature 302 °F		ASTM D638
 70.3 MPa
@Temperature 90.0 °C		10200 psi
@Temperature 194 °F		ASTM D638
 126 MPa
@Temperature 23.0 °C		18300 psi
@Temperature 73.4 °F		ASTM D638
 206 MPa
@Temperature -40.0 °C		29900 psi
@Temperature -40.0 °F		ASTM D638
Tensile Stress  20.5 MPa
@Strain 1.05 %,
Temperature 150 °C		2970 psi
@Strain 1.05 %,
Temperature 302 °F		ISO 527
 23.5 MPa
@Strain 0.960 %,
Temperature 120 °C		3410 psi
@Strain 0.960 %,
Temperature 248 °F		ISO 527
 23.5 MPa
@Strain 0.230 %,
Temperature 0.000 °C		3410 psi
@Strain 0.230 %,
Temperature 32.0 °F		ISO 527
 24.5 MPa
@Strain 0.260 %,
Temperature 40.0 °C		3550 psi
@Strain 0.260 %,
Temperature 104 °F		ISO 527
 25.6 MPa
@Strain 0.240 %,
Temperature -40.0 °C		3710 psi
@Strain 0.240 %,
Temperature -40.0 °F		ISO 527
 28.8 MPa
@Strain 0.960 %,
Temperature 90.0 °C		4180 psi
@Strain 0.960 %,
Temperature 194 °F		ISO 527
 30.4 MPa
@Strain 2.10 %,
Temperature 150 °C		4410 psi
@Strain 2.10 %,
Temperature 302 °F		ISO 527
 35.2 MPa
@Strain 0.600 %,
Temperature 60.0 °C		5110 psi
@Strain 0.600 %,
Temperature 140 °F		ISO 527
 35.9 MPa
@Strain 1.92 %,
Temperature 120 °C		5210 psi
@Strain 1.92 %,
Temperature 248 °F		ISO 527
 36.1 MPa
@Strain 3.16 %,
Temperature 150 °C		5240 psi
@Strain 3.16 %,
Temperature 302 °F		ISO 527
 40.4 MPa
@Strain 4.21 %,
Temperature 150 °C		5860 psi
@Strain 4.21 %,
Temperature 302 °F		ISO 527
 42.7 MPa
@Strain 2.88 %,
Temperature 120 °C		6190 psi
@Strain 2.88 %,
Temperature 248 °F		ISO 527
 44.0 MPa
@Strain 5.27 %,
Temperature 150 °C		6380 psi
@Strain 5.27 %,
Temperature 302 °F		ISO 527
 44.9 MPa
@Strain 0.460 %,
Temperature 0.000 °C		6510 psi
@Strain 0.460 %,
Temperature 32.0 °F		ISO 527
 45.0 MPa
@Strain 1.92 %,
Temperature 90.0 °C		6530 psi
@Strain 1.92 %,
Temperature 194 °F		ISO 527
 45.2 MPa
@Strain 0.530 %,
Temperature 40.0 °C		6560 psi
@Strain 0.530 %,
Temperature 104 °F		ISO 527
 46.8 MPa
@Strain 6.32 %,
Temperature 150 °C		6790 psi
@Strain 6.32 %,
Temperature 302 °F		ISO 527
 47.5 MPa
@Strain 3.84 %,
Temperature 120 °C		6890 psi
@Strain 3.84 %,
Temperature 248 °F		ISO 527
 49.4 MPa
@Strain 7.37 %,
Temperature 150 °C		7160 psi
@Strain 7.37 %,
Temperature 302 °F		ISO 527
 49.5 MPa
@Strain 0.480 %,
Temperature -40.0 °C		7180 psi
@Strain 0.480 %,
Temperature -40.0 °F		ISO 527
 51.3 MPa
@Strain 4.81 %,
Temperature 120 °C		7440 psi
@Strain 4.81 %,
Temperature 248 °F		ISO 527
 51.4 MPa
@Strain 8.43 %,
Temperature 150 °C		7450 psi
@Strain 8.43 %,
Temperature 302 °F		ISO 527
 53.0 MPa
@Strain 9.49 %,
Temperature 150 °C		7690 psi
@Strain 9.49 %,
Temperature 302 °F		ISO 527
 53.6 MPa
@Strain 2.88 %,
Temperature 90.0 °C		7770 psi
@Strain 2.88 %,
Temperature 194 °F		ISO 527
 54.2 MPa
@Strain 5.77 %,
Temperature 120 °C		7860 psi
@Strain 5.77 %,
Temperature 248 °F		ISO 527
 54.5 MPa
@Strain 10.5 %,
Temperature 150 °C		7900 psi
@Strain 10.5 %,
Temperature 302 °F		ISO 527
 56.5 MPa
@Strain 6.73 %,
Temperature 120 °C		8190 psi
@Strain 6.73 %,
Temperature 248 °F		ISO 527
 58.3 MPa
@Strain 7.69 %,
Temperature 120 °C		8460 psi
@Strain 7.69 %,
Temperature 248 °F		ISO 527
 58.4 MPa
@Strain 1.20 %,
Temperature 60.0 °C		8470 psi
@Strain 1.20 %,
Temperature 140 °F		ISO 527
 59.5 MPa
@Strain 3.84 %,
Temperature 90.0 °C		8630 psi
@Strain 3.84 %,
Temperature 194 °F		ISO 527
 59.6 MPa
@Strain 8.65 %,
Temperature 120 °C		8640 psi
@Strain 8.65 %,
Temperature 248 °F		ISO 527
 60.7 MPa
@Strain 9.61 %,
Temperature 120 °C		8800 psi
@Strain 9.61 %,
Temperature 248 °F		ISO 527
 63.2 MPa
@Strain 0.790 %,
Temperature 40.0 °C		9170 psi
@Strain 0.790 %,
Temperature 104 °F		ISO 527
 63.3 MPa
@Strain 4.81 %,
Temperature 90.0 °C		9180 psi
@Strain 4.81 %,
Temperature 194 °F		ISO 527
 63.9 MPa
@Strain 0.680 %,
Temperature 0.000 °C		9270 psi
@Strain 0.680 %,
Temperature 32.0 °F		ISO 527
 66.1 MPa
@Strain 5.77 %,
Temperature 90.0 °C		9590 psi
@Strain 5.77 %,
Temperature 194 °F		ISO 527
 68.1 MPa
@Strain 6.73 %,
Temperature 90.0 °C		9880 psi
@Strain 6.73 %,
Temperature 194 °F		ISO 527
 69.6 MPa
@Strain 7.69 %,
Temperature 90.0 °C		10100 psi
@Strain 7.69 %,
Temperature 194 °F		ISO 527
 70.6 MPa
@Strain 8.65 %,
Temperature 90.0 °C		10200 psi
@Strain 8.65 %,
Temperature 194 °F		ISO 527
 71.3 MPa
@Strain 9.61 %,
Temperature 90.0 °C		10300 psi
@Strain 9.61 %,
Temperature 194 °F		ISO 527
 72.1 MPa
@Strain 1.81 %,
Temperature 60.0 °C		10500 psi
@Strain 1.81 %,
Temperature 140 °F		ISO 527
 72.4 MPa
@Strain 0.720 %,
Temperature -40.0 °C		10500 psi
@Strain 0.720 %,
Temperature -40.0 °F		ISO 527
 77.2 MPa
@Strain 1.05 %,
Temperature 40.0 °C		11200 psi
@Strain 1.05 %,
Temperature 104 °F		ISO 527
 79.2 MPa
@Strain 2.41 %,
Temperature 60.0 °C		11500 psi
@Strain 2.41 %,
Temperature 140 °F		ISO 527
 81.3 MPa
@Strain 0.910 %,
Temperature 0.000 °C		11800 psi
@Strain 0.910 %,
Temperature 32.0 °F		ISO 527
 83.0 MPa
@Strain 3.01 %,
Temperature 60.0 °C		12000 psi
@Strain 3.01 %,
Temperature 140 °F		ISO 527
 84.6 MPa
@Strain 3.61 %,
Temperature 60.0 °C		12300 psi
@Strain 3.61 %,
Temperature 140 °F		ISO 527
 85.8 MPa
@Strain 4.21 %,
Temperature 60.0 °C		12400 psi
@Strain 4.21 %,
Temperature 140 °F		ISO 527
 86.5 MPa
@Strain 4.81 %,
Temperature 60.0 °C		12500 psi
@Strain 4.81 %,
Temperature 140 °F		ISO 527
 86.8 MPa
@Strain 5.41 %,
Temperature 60.0 °C		12600 psi
@Strain 5.41 %,
Temperature 140 °F		ISO 527
 87.2 MPa
@Strain 6.02 %,
Temperature 60.0 °C		12600 psi
@Strain 6.02 %,
Temperature 140 °F		ISO 527
 87.8 MPa
@Strain 1.32 %,
Temperature 40.0 °C		12700 psi
@Strain 1.32 %,
Temperature 104 °F		ISO 527
 93.0 MPa
@Strain 0.960 %,
Temperature -40.0 °C		13500 psi
@Strain 0.960 %,
Temperature -40.0 °F		ISO 527
 95.5 MPa
@Strain 1.58 %,
Temperature 40.0 °C		13900 psi
@Strain 1.58 %,
Temperature 104 °F		ISO 527
 96.6 MPa
@Strain 1.14 %,
Temperature 0.000 °C		14000 psi
@Strain 1.14 %,
Temperature 32.0 °F		ISO 527
 101 MPa
@Strain 1.84 %,
Temperature 40.0 °C		14600 psi
@Strain 1.84 %,
Temperature 104 °F		ISO 527
 104 MPa
@Strain 2.11 %,
Temperature 40.0 °C		15100 psi
@Strain 2.11 %,
Temperature 104 °F		ISO 527
 106 MPa
@Strain 2.37 %,
Temperature 40.0 °C		15400 psi
@Strain 2.37 %,
Temperature 104 °F		ISO 527
 107 MPa
@Strain 2.63 %,
Temperature 40.0 °C		15500 psi
@Strain 2.63 %,
Temperature 104 °F		ISO 527
 109 MPa
@Strain 1.37 %,
Temperature 0.000 °C		15800 psi
@Strain 1.37 %,
Temperature 32.0 °F		ISO 527
 112 MPa
@Strain 1.20 %,
Temperature -40.0 °C		16200 psi
@Strain 1.20 %,
Temperature -40.0 °F		ISO 527
 120 MPa
@Strain 1.60 %,
Temperature 0.000 °C		17400 psi
@Strain 1.60 %,
Temperature 32.0 °F		ISO 527
 129 MPa
@Strain 1.83 %,
Temperature 0.000 °C		18700 psi
@Strain 1.83 %,
Temperature 32.0 °F		ISO 527
 130 MPa
@Strain 1.44 %,
Temperature -40.0 °C		18900 psi
@Strain 1.44 %,
Temperature -40.0 °F		ISO 527
 136 MPa
@Strain 2.05 %,
Temperature 0.000 °C		19700 psi
@Strain 2.05 %,
Temperature 32.0 °F		ISO 527
 142 MPa
@Strain 2.28 %,
Temperature 0.000 °C		20600 psi
@Strain 2.28 %,
Temperature 32.0 °F		ISO 527
 146 MPa
@Strain 1.69 %,
Temperature -40.0 °C		21200 psi
@Strain 1.69 %,
Temperature -40.0 °F		ISO 527
 160 MPa
@Strain 1.93 %,
Temperature -40.0 °C		23200 psi
@Strain 1.93 %,
Temperature -40.0 °F		ISO 527
 172 MPa
@Strain 2.17 %,
Temperature -40.0 °C		24900 psi
@Strain 2.17 %,
Temperature -40.0 °F		ISO 527
 184 MPa
@Strain 2.41 %,
Temperature -40.0 °C		26700 psi
@Strain 2.41 %,
Temperature -40.0 °F		ISO 527
Elongation at Break  3.0 %
@Temperature -40.0 °C		3.0 %
@Temperature -40.0 °F		ASTM D638
 3.3 %
@Temperature 23.0 °C		3.3 %
@Temperature 73.4 °F		ASTM D638
 3.3 %
@Temperature 23.0 °C		3.3 %
@Temperature 73.4 °F		ISO 527
 7.0 %
@Temperature 90.0 °C		7.0 %
@Temperature 194 °F		ASTM D638
 7.5 %
@Temperature 150 °C		7.5 %
@Temperature 302 °F		ASTM D638
Tensile Modulus  2.70 GPa
@Temperature 150 °C		392 ksi
@Temperature 302 °F		ASTM D638
 3.28 GPa
@Temperature 90.0 °C		476 ksi
@Temperature 194 °F		ASTM D638
 9.30 GPa
@Temperature 23.0 °C		1350 ksi
@Temperature 73.4 °F		ISO 527
 9.31 GPa
@Temperature 23.0 °C		1350 ksi
@Temperature 73.4 °F		ASTM D638
 9.79 GPa
@Temperature -40.0 °C		1420 ksi
@Temperature -40.0 °F		ASTM D638
Flexural Strength  60.0 MPa
@Temperature 150 °C		8700 psi
@Temperature 302 °F		ASTM D790
 86.2 MPa
@Temperature 90.0 °C		12500 psi
@Temperature 194 °F		ASTM D790
 193 MPa
@Temperature 23.0 °C		28000 psi
@Temperature 73.4 °F		ASTM D790
 266 MPa
@Temperature -40.0 °C		38600 psi
@Temperature -40.0 °F		ASTM D790
Flexural Modulus  2.25 GPa
@Temperature 150 °C		326 ksi
@Temperature 302 °F		ASTM D790
 2.30 GPa
@Temperature 150 °C		334 ksi
@Temperature 302 °F		ISO 178
 3.00 GPa
@Temperature 93.0 °C		435 ksi
@Temperature 199 °F		ISO 178
 3.01 GPa
@Temperature 90.0 °C		437 ksi
@Temperature 194 °F		ASTM D790
 7.83 GPa
@Temperature 23.0 °C		1140 ksi
@Temperature 73.4 °F		ISO 178
 8.28 GPa
@Temperature 23.0 °C		1200 ksi
@Temperature 73.4 °F		ASTM D790
 8.90 GPa
@Temperature -40.0 °C		1290 ksi
@Temperature -40.0 °F		ASTM D790
 8.90 GPa
@Temperature -40.0 °C		1290 ksi
@Temperature -40.0 °F		ISO 178
Compressive Strength 148 MPa
@Temperature 23.0 °C		21500 psi
@Temperature 73.4 °F		ASTM D695
Izod Impact, Notched  1.01 J/cm
@Temperature -40.0 °C		1.89 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  9.60 J/cm
@Temperature -40.0 °C		18.0 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 9.60 J/cm
@Temperature 23.0 °C		18.0 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
@Temperature 23.0 °C		6.19 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Charpy Impact Unnotched  7.00 J/cm²
@Temperature 23.0 °C		33.3 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 8.60 J/cm²
@Temperature -30.0 °C		40.9 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  1.20 J/cm²
@Temperature -30.0 °C		5.71 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 1.40 J/cm²
@Temperature 23.0 °C		6.66 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm-cm
@Temperature 23.0 °C		1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance  1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+14 ohm
@Temperature 23.0 °C		1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.3
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.3
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.3
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.3
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.4
@Frequency 1000 Hz,
Temperature 23.0 °C		3.4
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.2
@Frequency 100 Hz,
Temperature 23.0 °C		4.2
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  12.0 kV/mm
@Thickness 3.20 mm,
Temperature 150 °C		305 kV/in
@Thickness 0.126 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 14.5 kV/mm
@Thickness 1.60 mm,
Temperature 150 °C		368 kV/in
@Thickness 0.0630 in,
Temperature 302 °F		500 V/s, in oil; Short Time; ASTM D149
 17.5 kV/mm
@Thickness 3.20 mm,
Temperature 95.0 °C		445 kV/in
@Thickness 0.126 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 21.5 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		546 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
 24.0 kV/mm
@Thickness 1.60 mm,
Temperature 95.0 °C		610 kV/in
@Thickness 0.0630 in,
Temperature 203 °F		500 V/s, in oil; Short Time; ASTM D149
 26.5 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		673 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		500 V/s, in oil; Short Time; ASTM D149
Dissipation Factor  0.010
@Frequency 1000 Hz,
Temperature 23.0 °C		0.010
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.015
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.015
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.015
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.015
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index 325 V
@Thickness 3.00 mm,
Temperature 23.0 °C		325 V
@Thickness 0.118 in,
Temperature 73.4 °F		UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  85.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		47.2 µin/in-°F
@Temperature -40.0 - 73.4 °F		ASTM E 831
 85.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		47.2 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 85.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		47.2 µin/in-°F
@Temperature -40.0 - 73.4 °F		ISO 11359-1/-2
 85.0 µm/m-°C
@Temperature 23.0 - 55.0 °C		47.2 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
 92.0 µm/m-°C
@Temperature 55.0 - 160 °C		51.1 µin/in-°F
@Temperature 131 - 320 °F		ASTM E 831
 92.0 µm/m-°C
@Temperature 55.0 - 160 °C		51.1 µin/in-°F
@Temperature 131 - 320 °F		ISO 11359-1/-2
 122 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		67.8 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ASTM E 831
 122 µm/m-°C
@Thickness 2.00 mm,
Temperature 23.0 - 55.0 °C		67.8 µin/in-°F
@Thickness 0.0787 in,
Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 254 °C489 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 237 °C459 °FISO 75-1/-2
 240 °C464 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 220 °C428 °FISO 75-1/-2
 220 °C428 °FASTM D648
UL RTI, Electrical  140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
UL RTI, Mechanical without Impact  140 °C
@Thickness 3.00 mm		284 °F
@Thickness 0.118 in		UL 746B
 140 °C
@Thickness 0.750 mm		284 °F
@Thickness 0.0295 in		UL 746B
 140 °C
@Thickness 1.50 mm		284 °F
@Thickness 0.0591 in		UL 746B
Flammability, UL94  HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		IEC 60695-11-10
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
Oxygen Index 22 %22 %ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 250 °C482 °F10°C/min; ISO 11357-1/-3
 280 °C536 °FOptimum
 270 - 290 °C518 - 554 °F
Mold Temperature >= 95.0 °C>= 203 °F
 110 °C230 °Foptimum
Drying Temperature 120 °C248 °F
Dry Time 4.00 hour4.00 hour
Moisture Content <= 0.020 %<= 0.020 %
 
Descriptive Properties
AdditiveImpact Modifier
AppearanceNatural Color
Drying RecommendedYes
FeaturesImpact Modified
 Impact Resistance, Good
 Stiffness, Good
 Strength, Good
 Thermal Aging Resistance, Good
FillerGlass fiber reinforcement
GenericPET
Heat StabilizedYes
Material StatusCurrent
Part Marking Code>PET-IGF30<ISO 11469
Polymer FamilyPolyester
Polymer TypePET
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
 Toughened Resins
Resin IdentificationPET-IGF30ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 Housings
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38922.html

免责声明: 本文 DuPont Performance Polymers Rynite® 408 NC010 PET 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4