- 密度 [g/cm3]: 1.58
- 缺口冲击强度: 11.0
- 断裂伸长率 [%]: 270
- 弯曲强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527-2/1A |
| Flexural Yield Strength | 270 MPa | 39200 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | ISO 180/1A |