- 密度 [g/cm3]: 1.58
- 缺口冲击强度: 0.801
- 弯曲模量 [MPa]: 11.0
- 热变形温度 [℃]: 240.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 | ||
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.160 % | 0.160 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 | ||
| 0.00700 cm/cm | 0.00700 in/in | ASTM D955 | |||
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 122 | 122 | ISO 2039-2 | ||
| Tensile Strength at Break | 159 MPa | 23100 psi | 5mm/min; ISO 527-2/1A | ||
| 165 MPa | 24000 psi | ASTM D638 | |||
| Elongation at Break | 2.30 % | 2.30 % | 5mm/min; ISO 527-2/1A | ||
| 2.00 % @Temperature 22.8 °C | 2.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 11.1 GPa | 1610 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 229 MPa | 33200 psi | ISO 178 | ||
| 245 MPa | 35500 psi | ASTM D790 | |||
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 | ||
| 9.65 GPa @Temperature 22.8 °C | 1400 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 8.80 kJ/m² | 4.19 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eU | ||
| 2.80 J/cm² @Temperature -30.0 °C | 13.3 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA | ||
| 0.880 J/cm² @Temperature -30.0 °C | 4.19 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | ASTM D257 | ||
| 7.00e+16 ohm-cm | 7.00e+16 ohm-cm | IEC 60093 | |||
| Surface Resistance | 3.10e+14 ohm | 3.10e+14 ohm | ASTM D257 | ||
| 3.00e+15 ohm | 3.00e+15 ohm | IEC 60093 | |||
| Dielectric Constant | 2.83 @Frequency 100 Hz | 2.83 @Frequency 100 Hz | IEC 60250 | ||
| 3.10 @Frequency 10000 Hz | 3.10 @Frequency 10000 Hz | ASTM D150 | |||
| 3.20 @Frequency 1000 Hz | 3.20 @Frequency 1000 Hz | ASTM D150 | |||
| 3.46 @Frequency 1.00e+6 Hz | 3.46 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 22.2 kV/mm | 565 kV/in | short term; ASTM D149 | ||
| 32.0 kV/mm | 813 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0100 @Frequency 1000 Hz | 0.0100 @Frequency 1000 Hz | ASTM D150 | ||
| 0.0120 @Frequency 100 Hz | 0.0120 @Frequency 100 Hz | IEC 60250 | |||
| 0.0140 @Frequency 1.00e+6 Hz | 0.0140 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 0.0160 @Frequency 10000 Hz | 0.0160 @Frequency 10000 Hz | ASTM D150 | |||
| Arc Resistance | 125 sec | 125 sec | ASTM D495 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| 175 V | 175 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 18.0 µm/m-°C | 10.0 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 244 °C | 471 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Transformation Temperature, Tg | 73.0 °C | 163 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ISO 75-1, -2 | ||
| 224 °C | 435 °F | ASTM D648 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| Oxygen Index | 25.0 % | 25.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 110 - 121 °C | 230 - 250 °F | Cavity temperature | |||
| Feed Temperature | 255 - 265 °C | 491 - 509 °F | |||
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Middle Barrel Temperature | 270 - 275 °C | 518 - 527 °F | |||
| Front Barrel Temperature | 275 - 280 °C | 527 - 536 °F | |||
| Nozzle Temperature | 275 - 290 °C | 527 - 554 °F | |||
| Zone 1 | 255 - 265 °C | 491 - 509 °F | |||
| Zone 2 | 260 - 275 °C | 500 - 527 °F | |||
| Zone 3 | 260 - 275 °C | 500 - 527 °F | |||
| Zone 4 | 265 - 280 °C | 509 - 536 °F | |||
| Die Temperature | 270 - 290 °C | 518 - 554 °F | |||
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |||
| 270 - 300 °C | 518 - 572 °F | ||||
| 285 °C | 545 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 110 - 121 °C | 230 - 250 °F | |||
| 135 °C | 275 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 275 mm/sec | 10.8 in/sec | ISO 294 | ||
| Drying Temperature | 130 - 140 °C | 266 - 284 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Hold Pressure | 60.0 MPa | 8700 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.172 MPa | 0.000 - 25.0 psi | |||
| Screw Speed | 50.0 - 75.0 rpm | 50.0 - 75.0 rpm | |||
| Hot-Working Temperature | 260 - 290 °C | 500 - 554 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Medium/Fast Injection Speed | ||||