- 熔体流动速率 [g/10min]: 7.5
- 缺口冲击强度: 4.02
- 断裂伸长率 [%]: 5.00
- 弯曲强度 [MPa]: 7.85
- 弯曲模量 [MPa]: 0.0715
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ASTM D792 |
| Melt Flow | 7.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 40 | 40 | ASTM D2240 |
| Tensile Strength, Ultimate | 7.85 MPa | 1140 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Yield Strength | 5.00 MPa | 725 psi | ASTM D790 |
| Flexural Modulus | 0.0715 GPa | 10.4 ksi | ASTM D790 |
| Izod Impact, Notched | 4.02 J/cm | 7.53 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 120 °C | 248 °F | ASTM D3418 |