- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 0.480
- 热变形温度 [℃]: 51.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| ESCR 100% Igepal® | >= 1500 hour | >= 1500 hour | Condition C; ASTM D1693 | ||
| ESCR 10% Igepal® | >= 1500 hour | >= 1500 hour | Condition B; ASTM D1693 | ||
| Melt Flow | 15 g/10 min | 15 g/10 min | Condition 190/21.6, HLMI; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 55 | 55 | ASTM D2240 | ||
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | 2 in/min, Type IV bar; ASTM D638 | ||
| Elongation at Break | 750 % | 750 % | 2 in/min, Type IV bar; ASTM D638 | ||
| Flexural Modulus | 0.480 GPa | 69.6 ksi | Tangent, 16:1 span:depth,0.5in/min; ASTM D790 | ||
| Tensile Impact Strength | 800 kJ/m² | 381 ft-lb/in² | Type S bar; ASTM D1822 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 51.0 °C | 124 °F | Method A; ASTM D648 | ||
| Vicat Softening Point | 104 °C | 219 °F | Loading 1, Rate A; ASTM D1525 | ||
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | Type A clamp, type 1 specimen; ASTM D746 | ||
| Descriptive Properties | |||||
| SP-NCTL | Min 1000 | Single-point notched constant tensile load | |||