- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9215
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9215 g/cc | 0.03329 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 1000 ppm | 1000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.45 MPa | 1516 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.62 MPa | 1686 psi | ASTM D882 |
| Film Elongation at Break, MD | 623 % | 623 % | ASTM D882 |
| Film Elongation at Break, TD | 683 % | 683 % | ASTM D882 |
| Secant Modulus, MD | 0.192364 GPa | 27.9004 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.228216 GPa | 33.1005 ksi | 2% Secant; ASTM D882 |
| Impact | 70 | 70 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1173 | 1173 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 1196 | 1196 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Elmendorf Tear Strength MD | 811 g | 811 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1230 g | 1230 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.96 g/micron | 405.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.2 g/micron | 615 g/mil | ASTM D1922 |
| Dart drop Test | 311 g | 0.686 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.6 MPa | 5170 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.12 MPa | 4223 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 64.9 % | 64.9 % | 45°; ASTM D2457 |