- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.342 MPa | 1355 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.970 MPa | 1446 psi | ASTM D882 |
| Film Elongation at Break, MD | 601 % | 601 % | ASTM D882 |
| Film Elongation at Break, TD | 651 % | 651 % | ASTM D882 |
| Secant Modulus, MD | 0.158131 GPa | 22.9354 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.185241 GPa | 26.8674 ksi | 2% Secant; ASTM D882 |
| Impact | 131 | 131 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1049 | 1049 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 1079 | 1079 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Elmendorf Tear Strength MD | 916 g | 916 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1210 g | 1210 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.0 g/micron | 458 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 23.8 g/micron | 605 g/mil | ASTM D1922 |
| Dart drop Test | 609 g | 1.34 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.45 MPa | 5141 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.59 MPa | 4147 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D1003 |
| Gloss | 68 % | 68 % | 45°; ASTM D2457 |