- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.538 g/cc | 0.0194 lb/in³ | ASTM D1895 | ||
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 | ||
| Thickness | 25.0 microns | 0.984 mil | As Tested | ||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Elmendorf Tear Strength, MD | 35.0 g/micron @Thickness 0.0250 mm | 889 g/mil @Thickness 0.000984 in | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 26.0 g/micron @Thickness 0.0250 mm | 660 g/mil @Thickness 0.000984 in | ASTM D1922 | ||
| Dart Drop | 4.20 g/micron @Thickness 0.0250 mm | 107 g/mil @Thickness 0.000984 in | ASTM D1709 A | ||
| Dart drop Test | 105 g | 0.232 lb | F50; ASTM D1709 A | ||
| Film Tensile Strength at Break, MD | 34.0 MPa @Thickness 0.0250 mm | 4930 psi @Thickness 0.000984 in | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 26.0 MPa @Thickness 0.0250 mm | 3770 psi @Thickness 0.000984 in | ASTM D882 | ||
| 1% Secant Modulus, MD | 193 MPa @Thickness 0.0250 mm | 28000 psi @Thickness 0.000984 in | ASTM D882 | ||
| 1% Secant Modulus, TD | 221 MPa @Thickness 0.0250 mm | 32100 psi @Thickness 0.000984 in | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Equate Test Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003 | ||
| Gloss | 65 % | 65 % | 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Blow-up Ratio (BUR) | 2.0 | 2.0 | 2:1 As Tested | ||
| Descriptive Properties | |||||
| Puncture Energy | 70 J/mm | Equate Test Method | |||