- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.902
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.0760 GPa | 11.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0970 GPa | 14.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 510 g | 510 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 850 g | 850 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 20.1 g/micron | 510 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.5 g/micron | 850 g/mil | ASTM D1922 |
| Dart Drop | 17.3 g/micron | 440 g/mil | ASTM D1709 |
| Dart drop Test | 440 g | 0.970 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | >= 12.0 MPa | >= 1740 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 82 % | 82 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 165 - 205 °C | 329 - 401 °F | |