- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.924
- 弯曲模量 [MPa]: 0.115
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 9.0 % | 9.0 % | AT Plastics PTM-39 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 94 | 94 | ASTM D2240 |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 692 % | 692 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.115 GPa | 16.7 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 98.0 °C | 208 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |