- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
- 弯曲模量 [MPa]: 0.215
- 脆化温度 [℃]: -82.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95.5 | 95.5 | ASTM D2240 |
| Hardness, Shore D | 47 | 47 | ASTM D2240 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 550 % | 550 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.215 GPa | 31.2 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 234 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Brittleness Temperature | -82.0 °C | -116 °F | ASTM D746 |