- 熔体流动速率 [g/10min]: 22.0
- 弯曲模量 [MPa]: 0.0433
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Vinyl Acetate Content | 19 % | 19 % | AT Plastics PTM-39 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C | 22 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| Hardness, Shore D | 30 | 30 | ASTM D2240 |
| Tensile Strength at Break | 10.6 MPa | 1540 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 740 % | 740 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0433 GPa | 6.28 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 83.0 °C | 181 °F | DSC; ASTM D3417 |
| Vicat Softening Point | 56.0 °C | 133 °F | ASTM D1525 |