- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 400 % | 400 % | ISO 527-3 |
| Film Elongation at Break, TD | 650 % | 650 % | ISO 527-3 |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | TD; ASTM D882-A |
| 0.200 GPa | 29.0 ksi | MD; ASTM D882-A | |
| Elmendorf Tear Strength, MD | 7.65 g/micron | 194 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 5.097 g/micron | 129.5 g/mil | ISO 6383/2 |
| Dart drop Test | 80.0 g @Thickness 0.0400 mm | 0.176 lb @Thickness 0.00157 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 111 °C | 232 °F | ISO 11357-3 |
| Vicat Softening Point | 94.0 °C | 201 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 110 % | 110 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 140 - 180 °C | 284 - 356 °F | |