- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.919
- 缺口冲击强度: 69.4
- 拉伸强度 [MPa]: 10.7
- 弯曲强度 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | |
| Viscosity | 76000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 76000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 176000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 176000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 305000 cP @Shear Rate 300 1/s, Temperature 190 °C | 305000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 13.1 MPa | 1900 psi | |
| Tensile Strength, Yield | 10.7 MPa | 1550 psi | |
| Elongation at Break | 480 % | 480 % | |
| Modulus of Elasticity | 0.193 GPa | 28.0 ksi | Molded Sample 2% Secant Modulus |
| Izod Impact, Notched (ISO) | 69.4 kJ/m² @Temperature -50.0 °C | 33.0 ft-lb/in² @Temperature -58.0 °F | |
| Tensile Impact Strength | 315 kJ/m² | 150 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | |