- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 13.0 microns | 0.512 mil | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg | 6.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.1 MPa | 1750 psi | |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | |
| Film Elongation at Break, MD | 190 % | 190 % | |
| Film Elongation at Break, TD | 500 % | 500 % | |
| Coefficient of Friction | 0.10 | 0.10 | |
| Elmendorf Tear Strength MD | 140 g | 140 g | |
| Elmendorf Tear Strength TD | 95 g | 95 g | |
| Elmendorf Tear Strength, MD | 10.8 g/micron | 274 g/mil | |
| Elmendorf Tear Strength, TD | 7.30 g/micron | 185 g/mil | |
| Dart Drop | 1.40 g/micron | 35.6 g/mil | |
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | |
| Film Tensile Strength at Break, TD | 13.4 MPa | 1940 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 6.7 % | 6.7 % | |
| Gloss | 71 % | 71 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 218 °C | 424 °F | Film extrusion temperature |