- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.1 MPa | 1750 psi | |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | |
| Coefficient of Friction | 0.20 | 0.20 | |
| Elmendorf Tear Strength MD | 300 g | 300 g | |
| Elmendorf Tear Strength TD | 250 g | 250 g | |
| Elmendorf Tear Strength, MD | 12.0 g/micron | 305 g/mil | |
| Elmendorf Tear Strength, TD | 10.0 g/micron | 254 g/mil | |
| Optical Properties | Metric | English | Comments |
| Haze | 3.8 % | 3.8 % | |
| Gloss | 77 % | 77 % | 45° |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 188 °C | 370 °F | Film extrusion temperature |