- 熔体流动速率 [g/10min]: 0.25
- 密度 [g/cm3]: 0.918
- 弯曲模量 [MPa]: 0.234
- 热变形温度 [℃]: 42.0
- 脆化温度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.25 g/10 min | 0.25 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 50 | 50 | ASTM D2240 |
| Tensile Strength at Break | 14.5 MPa | 2100 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 0.234 GPa | 34.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |