- 拉伸强度 [MPa]: 17.9
- 弯曲模量 [MPa]: 0.724
- 热变形温度 [℃]: 52.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.942 g/cc | 0.942 g/cc | ASTM D792 | ||
| ESCR 100% Igepal® | >= 500 hour | >= 500 hour | ASTM D1693 | ||
| Melt Index of Compound | 6.0 g/10 min | 6.0 g/10 min | 2.16/190; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 17.9 MPa | 2600 psi | 2"/min; ASTM D638 | ||
| Elongation at Break | 400 % | 400 % | 2"/min; ASTM D638 | ||
| Flexural Modulus | 0.724 GPa | 105 ksi | at 1% secant modulus; ASTM D790 | ||
| Impact Test | 56.9 J @Thickness 3.17 mm, Temperature -40.0 °C | 42.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM impact | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 52.0 °C | 126 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| UV Stabilization | UV-8 | ||||