- 缺口冲击强度: 0.534
- 拉伸强度 [MPa]: 24.1
- 弯曲模量 [MPa]: 0.965
- 脆化温度 [℃]: -95.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.965 g/cc | 0.965 g/cc | ASTM D792 |
| ESCR 100% Igepal® | 1.0 hour | 1.0 hour | Condition B; ASTM D1693 |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 60 | 60 | ASTM D2240 |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | 2"/min; ASTM D638 |
| Elongation at Break | >= 50 % | >= 50 % | 2"/min; ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | 1% secant; ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 31.2 J | 23.0 ft-lb | F50 at -40°C; ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -95.0 °C | -139 °F | ASTM D746 |