- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.946
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in³ | ISO 1183 |
| Melt Flow | 0.20 g/10 min @Load 5.00 kg, Temperature 190 °C | 0.20 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 |
| High Load Melt Index | 6.0 g/10 min @Load 21.6 kg, Temperature 190 °C | 6.0 g/10 min @Load 47.6 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 450 % | 450 % | ISO 527-3 |
| Secant Modulus, MD | 0.600 GPa | 87.0 ksi | 0.05-1.05%; ISO 527-3 |
| Secant Modulus, TD | 0.700 GPa | 102 ksi | 0.05-1.05%; ISO 527-3 |
| Impact | 38 | 38 | Puncture Resistance, force (N); ASTM 5748 |
| Puncture Energy | 1.50 J | 1.11 ft-lb | ASTM 5748 |
| Tear Strength, Total | 0.200 N | 0.0450 lb (f) | MD; ISO 6383/2 |
| 1.00 N | 0.225 lb (f) | TD; ISO 6383/2 | |
| Elmendorf Tear Strength, MD | 1.36 g/micron | 34.5 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 20.38 g/micron | 517.7 g/mil | ISO 6383/2 |
| Dart Drop | 30.0 g/micron | 762 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 75.0 MPa | 10900 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | >= 131 °C | >= 268 °F | ISO 11357/03 |
| Vicat Softening Point | 125 °C | 257 °F | A (10N); ISO 306 |