- 熔体流动速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.942
- 缺口冲击强度: 21.0
- 拉伸强度 [MPa]: 19.3
- 弯曲模量 [MPa]: 69.0
- 脆化温度 [℃]: -118.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D4883 | ||
| Environmental Stress Crack Resistance | 5000 hour | 5000 hour | > 5000 hrs.; ASTM D1693 | ||
| Oxidative Induction Time (OIT) | 20 min | 20 min | @210 C > 20 Min; ASTM D 3895 | ||
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | @ 190 C/2160g; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 | 64 | ASTM D2240 | ||
| Tensile Strength at Break | 31.0 MPa | 4500 psi | 2 in/min; ASTM D638 | ||
| Tensile Strength, Yield | 19.3 MPa | 2800 psi | 2 in/min; ASTM D638 | ||
| Elongation at Break | 800 % | 800 % | >800% 2 in/min; ASTM D638 | ||
| Flexural Modulus | 69.0 GPa | 10000 ksi | ASTM D790 | ||
| Izod Impact, Notched (ISO) | 21.0 kJ/m² | 10.0 ft-lb/in² | ASTM D256 | ||
| Hydrostatic Design Basis | 6.89 MPa | 1000 psi | @ 60 C; ASTM D2837 | ||
| 8.62 MPa | 1250 psi | @ 23 C; ASTM D2837 | |||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 120 °C | 248 °F | ASTM D1525 | ||
| Brittleness Temperature | -118 °C | -180 °F | ASTM D746 | ||
| Descriptive Properties | |||||
| process | Pipe Extrusion | ||||
| region | US & Canada | ||||