- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.958
- 拉伸强度 [MPa]: 31.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in³ | ISO 1183 |
| Water Vapor Transmission | 4.10 g/m²/day @Temperature 38.0 °C | 0.264 g/100 in²/day @Temperature 100 °F | 90% humidity; ASTM F 1249 |
| Oxygen Transmission Rate | 2210 cc/m²/day @Temperature 23.0 °C | 142 cc/100 in²/day @Temperature 73.4 °F | wet; ASTM D3985 |
| Molecular Weight | 130000 g/mol | 130000 g/mol | distribution: 9 Mw/Mn; GPC |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | MD; ISO 527-3 |
| 35.0 MPa | 5080 psi | TD; ISO 527-3 | |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527-3 |
| Film Elongation at Break, TD | 500 % | 500 % | ISO 527-3 |
| Tensile Modulus | 0.760 GPa | 110 ksi | MD; ASTM D882-A |
| 0.940 GPa | 136 ksi | TD; ASTM D882-A | |
| Puncture Energy | 1.00 J | 0.738 ft-lb | 40N; ASTM D5748 |
| Coefficient of Friction | 0.27 | 0.27 | Dynamic; ISO 8295 |
| Dart drop Test | 50.0 g | 0.110 lb | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 132 °C | 270 °F | ISO 11357-3 |
| Vicat Softening Point | 129 °C @Load 1.02 kg | 264 °F @Load 2.25 lb | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 56 % | 56 % | ASTM D1003 |
| Gloss | 24 % | 24 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 °C | 374 °F | cylinder temperature |
| Zone 1 | 160 °C | 320 °F | |
| Zone 2 | 170 °C | 338 °F | |
| Zone 3 | 180 °C | 356 °F | |
| Zone 4 | 190 °C | 374 °F | |
| Die Temperature | 190 °C | 374 °F | |
| Melt Temperature | >= 200 °C | >= 392 °F | |