- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.964
- 拉伸强度 [MPa]: 27.0
- 热变形温度 [℃]: 77.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.964 g/cc | 0.0348 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 63 | 63 | ISO 868 | ||
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C | 2.86 ft-lb/in² @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 275 °C | 410 - 527 °F | |||
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |||
| Descriptive Properties | |||||
| Hold Pressure | as low as possible | ||||
| Injection Velocity | as high as possible | ||||