| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.957 g/cc | 0.957 g/cc | ASTM D1505/D792 |
| ESCR 100% Igepal® | 15 hour @Temperature 50.0 °C | 15 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| ESCR 10% Igepal® | 10 hour @Temperature 50.0 °C | 10 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| Melt Flow | 7.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Flexural Modulus, 1% Secant | 1360 MPa | 197000 psi | ASTM D790 |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |