- 熔体流动速率 [g/10min]: 0.38
- 缺口冲击强度: 3.0
- 拉伸强度 [MPa]: 33.0
- 热变形温度 [℃]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.966 g/cc | 0.966 g/cc | ASTM D1505/D792 |
| ESCR 100% Igepal® | 32 hour @Temperature 50.0 °C | 32 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| ESCR 10% Igepal® | 23 hour @Temperature 50.0 °C | 23 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| Melt Flow | 0.38 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.38 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 32 g/10 min @Load 21.6 kg, Temperature 190 °C | 32 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength at Break | 29.0 MPa | 4210 psi | ASTM D638 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| 2% Secant Modulus | 1.36 GPa | 197 ksi | ASTM D790 |
| Izod Impact, Notched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |