- 熔体流动速率 [g/10min]: 4.5
- 缺口冲击强度: 7.6
- 拉伸强度 [MPa]: 23.0
- 弯曲模量 [MPa]: 1080
- 热变形温度 [℃]: 70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.944 g/cc | 0.944 g/cc | ASTM D792 |
| ESCR 100% Igepal® | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
| ESCR 10% Igepal® | 185 hour @Temperature 50.0 °C | 185 hour @Temperature 122 °F | h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
| Melt Flow | 4.5 g/10 min @Load 21.6 kg, Temperature 190 °C | 4.5 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | ASTM D2240 |
| Tensile Strength at Break | 42.0 MPa | 6090 psi | ASTM D638 |
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ASTM D638 |
| Flexural Modulus, 1% Secant | 1080 MPa | 157000 psi | ASTM D790 |
| Izod Impact, Notched | 7.60 J/cm | 14.2 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |