- 熔体流动速率 [g/10min]: 0.34
- 缺口冲击强度: 2.1
- 拉伸强度 [MPa]: 32.0
- 热变形温度 [℃]: 79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.961 g/cc | 0.961 g/cc | ASTM D792 |
| ESCR 100% Igepal® | 19 hour @Temperature 50.0 °C | 19 hour @Temperature 122 °F | h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
| ESCR 10% Igepal® | 17 hour @Temperature 50.0 °C | 17 hour @Temperature 122 °F | h/F50; Compression molded 2mm notched-plaques; ASTM D1693 |
| Melt Flow | 0.34 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.34 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 28 g/10 min @Load 21.6 kg, Temperature 190 °C | 28 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | ASTM D638 |
| Tensile Strength, Yield | 32.0 MPa | 4640 psi | ASTM D638 |
| 2% Secant Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 2.10 J/cm | 3.93 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 79.0 °C | 174 °F | ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |